Tarnamid® T-27
- Chemical Family
- Polyamides
Medium viscosity polyamide 6 ISO 1874-1: PA 6, MN, 14-030
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Consumer Goods — Apparel; Consumer Goods — Other Consumer Goods Applications
Industrial — Leather & Textiles
- Textile Manufacturing
Personal Care — Packaging & Accessories
- Applicators & Accessories
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Tarnamid
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 2400.0 - 2400.0 MPa
- Processing Methods
- Compounding, Injection Molding
- Color
- Natural
- Markets
- Consumer Goods
- Industrial
- Personal Care
- Flame Rating
- IEC 60695-11-10 V2
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Food Contact Acceptable
- Medium Viscosity
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Fibers
- Monofilaments
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Compounding
- Injection Molding
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 2800 / 1100 | MPa | ISO 527 |
| Yield stress | 78 / 45 | MPa | ISO 527 |
| Flexural modulus, 23° | 2400 / 900 | MPa | ISO 178 |
| Strain at Break | min. 50 / min. 50 | % | ISO 527 |
| Charpy impact strength (-30°) | N / N | kJ/m2 | ISO 179/1eU |
| Charpy impact strength (+23°) | N / N | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (+23°) | 5.0/12.0 | kJ/m2 | ISO 179/1eA |
| Charpy notched impact strength (-30°) | 3.0/3.0 | kJ/m2 | ISO 179/1eA |
| Izod notched impact strength, +23° | 4.0/10.0 | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 140 / 60 | MPa | ISO 2039-1 |
Table 2 of 6
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 120 | cm3/10min | ISO 1133 |
| Melt Volume Flow Rate - MVR (275°C/5 kg) | 120 / * | cm3/10 min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 1 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 4 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 4/1 | % | ISO 294-4 |
| Molding shrinkage - normal | 1.4 / * | % | ISO 294-4, 2577 |
| Molding shrinkage - parallel | 1.4 / * | % | ISO 294-4, 2577 |
| Water Absorption (23/sat.) | 9.5 | % | ISO 62 |
| Moisture Absorption (23°C/50% RH) | 3 | % | ISO 62 |
| Relative Viscosity (H2SO4/25°C) | 2.7 | — | ISO 307 |
| Density | 1140 / - | kg/m3 | ISO 1183 |
Table 3 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (parallel) | 110 / * | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 120 / * | E-6/K | ISO 11359-1/-2 |
| Delfection Temperature Under Load (1.8 MPa) | 60 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 60 / * | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 221 | °C | ISO 11357-1 |
| Vicat Softening Temperature (50 N) | 195 | °C | ISO 306 |
| Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 / * | mm | — |
| Vicat softening temperature | 195 / * | °C | ISO 306 |
| Burning Behavior at thickness | V-2 / * | class | IEC 60695-11-10 |
Table 4 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index - CTI | 600 | V | UL 746 |
| Surface Resistivity | 1.0e+15 | ohm | STN 34 6460 |
| Volume Resistivity | 1.0e+15 | ohm.m | ASTM D 257 |
Table 5 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability - Glow Wire Test | 750 | °C | IEC-60695-2-12 |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 9.5 / * | % | Sim. to ISO 62 |
| Humidity absorption | 3 / * | % | Sim. to ISO 62 |