Tarnamid® T-27 GF 10 GB 20
- Chemical Family
- Polyamides
Tarnamid® T-27 GF 10 GB 20 is a 10% glass fiber and 20% glass spheres reinforced polyamide 6 compound, heat stabilized.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Other Building Materials
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Tarnamid
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Bead, Glass Fiber
- Glass Bead
- Glass Fiber
- Flexural Modulus
- 4900.0 - 4900.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- Heat Stabilized
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Construction Applications
- Electrical/Electronic Applications
- Household Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 110 / 60 | MPa | ISO 527 |
| Tensile Modulus | 5800 / 3400 | MPa | ISO 527 |
| Strain at break | 5.0/8.0 | % | ISO 527 |
| Flexural modulus, 23° | 4900 / 2600 | MPa | ISO 178 |
| Charpy notched impact strength (-30°) | 3.0/5.0 | kJ/m2 | ISO 179/1eA |
| Charpy notched impact strength (+23°) | 3.5 / 7 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (-30°) | 30 / 80 | kJ/m2 | ISO 179/1eU |
| Charpy impact strength (+23°) | 40 / 100 | kJ/m2 | ISO 179/1eU |
| Izod notched impact strength, +23° | 4.0/8.0 | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 210 / 95 | MPa | ISO 2039-1 |
Table 2 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 40 | cm3/10min | ISO 1133 |
| Melt Volume Flow Rate - MVR (275°C/5 kg) | 40 / * | cm3/10 min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 0 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 7/1 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 3 | % | ISO 294-4 |
| Molding shrinkage - parallel | 0.7 / * | % | ISO 294-4, 2577 |
| Molding shrinkage - normal | 1.3 / * | % | ISO 294-4, 2577 |
| Density | 1350 / - | kg/m3 | ISO 1183 |
Table 3 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (normal) | 110 / * | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (parallel) | 40 / * | E-6/K | ISO 11359-1/-2 |
| Delfection Temperature Under Load (1.8 MPa) | 70 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 70 / * | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 221 | °C | ISO 11357-1 |
| Vicat Softening Temperature (50 N) | 210 | °C | ISO 306 |
| Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 / * | mm | — |
| Vicat softening temperature | 210 / * | °C | ISO 306 |
| Burning Behavior at thickness | HB / * | class | IEC 60695-11-10 |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index - CTI | 525 | V | IEC 60112 |
| Surface Resistivity | 1.0e+15 | ohm | STN 34 6460 |
| Volume Resistivity | 1.0e+15 | ohm.m | ASTM D 257 |
Table 5 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability - Glow Wire Test | 650 | °C | IEC-60695-2-12 |