Tarnamid® T- 29 MS
- Chemical Family
- Polyamides
It is medium-high viscosity general purpose polyamide 6, containing release agent.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Other Building Materials
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Tarnamid
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 2300.0 - 2300.0 MPa
- Additives Included
- Mold Release Agent
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- IEC 60695-11-10 V2
- Technology
- Plastics
- Material Features
- Broad Range of Viscosity
- General Purpose
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Construction Applications
- Electrical/Electronic Applications
- General Purpose
- Household Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 3100 / 1500 | MPa | ISO 527 |
| Yield stress | 82 / 45 | MPa | ISO 527 |
| Flexural modulus, 23° | 2300 / 1100 | MPa | ISO 178 |
| Charpy impact strength (+23°) | N / N | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (-30°) | 3 / - | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (-30°) | N / - | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (+23°) | 5.5 / 13 | kJ/m2 | ISO 179/1eA |
| Strain at Break | 40 / min. 50 | % | ISO 527 |
| Izod notched impact strength, +23° | 5.0/13.0 | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 165 / 75 | MPa | ISO 2039-1 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (275°C/5 kg) | 120 / * | cm3/10 min | ISO 1133 |
| Molding shrinkage - normal | 1.4 / * | % | ISO 294-4, 2577 |
| Molding shrinkage - parallel | 1.4 / * | % | ISO 294-4, 2577 |
| Density | 1140 / - | kg/m3 | ISO 1183 |
Table 3 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (parallel) | 110 / * | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 120 / * | E-6/K | ISO 11359-1/-2 |
| Temperature of deflection under load (1.80 Mpa) | 60 / * | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
| Thickness tested | 1.6 / * | mm | — |
| Vicat softening temperature | 195 / * | °C | ISO 306 |
| Burning Behavior at thickness | V-2 / * | class | IEC 60695-11-10 |
| Burning Behavior at 1.5 mm nominal thickness | V-2 / * | class | IEC 60695-11-10 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 9.5 / * | % | Sim. to ISO 62 |
| Humidity absorption | 3 / * | % | Sim. to ISO 62 |