Tarnamid® T-30 MCS 18
- Chemical Family
- Polyamides
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Other Building Materials
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Tarnamid
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 2100.0 - 2100.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Plastics and Elastomers End Uses
- Automotive Applications
- Construction Applications
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 2600 / 1000 | MPa | ISO 527 |
| Yield stress | 72 / 40 | MPa | ISO 527 |
| Flexural modulus, 23° | 2100 / 700 | MPa | ISO 178 |
| Charpy impact strength (-30°) | N / N | kJ/m2 | ISO 179/1eU |
| Charpy impact strength (+23°) | N / N | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (+23°) | 12.0/20.0 | kJ/m2 | ISO 179/1eA |
| Charpy notched impact strength (-30°) | 8.0/10.0 | kJ/m2 | ISO 179/1eA |
| Strain at Break | 50 / min. 50 | % | ISO 527 |
| Ball indentation hardness | 135 / 60 | MPa | ISO 2039-1 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (275°C/5 kg) | 20 / * | cm3/10 min | ISO 1133 |
| Molding shrinkage - normal | 1.5 / * | % | ISO 294-4, 2577 |
| Molding shrinkage - parallel | 2.0 / * | % | ISO 294-4, 2577 |
| Density | 1110 / - | kg/m3 | ISO 1183 |
Table 3 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temperature of deflection under load (1.80 Mpa) | 55 / * | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 / * | mm | — |
| Vicat softening temperature | 180 / * | °C | ISO 306 |
| Burning Behavior at thickness | HB / * | class | IEC 60695-11-10 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 9.5 / * | % | Sim. to ISO 62 |
| Humidity absorption | 2.5 / * | % | Sim. to ISO 62 |