Tarnamid® T- 27 Z1
- Chemical Family
- Polyamides
Poliamid 6 impact modified grade. ISO 1874-1: PA 6-HI, MR, 14-020
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Other Building Materials
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Tarnamid
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 2200.0 - 2200.0 MPa
- Additives Included
- Impact Modifier
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- Impact Modified
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Construction Applications
- Electrical/Electronic Applications
- Household Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 2800 / - | MPa | ISO 527 |
| Yield stress | 72 / - | MPa | ISO 527 |
| Strain at break | 40 / - | % | ISO 527 |
| Flexural modulus, 23° | 2200 / - | MPa | ISO 178 |
| Charpy impact strength (+23°) | N / - | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (+23°) | 10 / - | kJ/m2 | ISO 179/1eA |
| Izod notched impact strength, +23° | 10 / - | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 150 / - | MPa | ISO 2039-1 |
Table 2 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 110 | cm3/10min | ISO 1133 |
| Melt Volume Flow Rate - MVR (275°C/5 kg) | 110 / * | cm3/10 min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 7/- | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 0 | % | ISO 294-4 |
| Molding shrinkage - parallel | 0.7 / * | % | ISO 294-4, 2577 |
| Water Absorption (23/sat.) | 9.5 | % | ISO 62 |
| Moisture Absorption (23°C/50% RH) | 2.8 | % | ISO 62 |
| Density | 1110 / - | kg/m3 | ISO 1183 |
Table 3 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Delfection Temperature Under Load (1.8 MPa) | 55 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 55 / * | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 221 | °C | ISO 11357-1 |
| Vicat Softening Temperature (50 N) | 195 | °C | ISO 306 |
| Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 / * | mm | — |
| Vicat softening temperature | 195 / * | °C | ISO 306 |
| Burning Behavior at thickness | HB / * | class | IEC 60695-11-10 |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index - CTI | 600 | V | UL 746 |
| Surface Resistivity | 1.0e+15 | ohm | STN 34 6460 |
| Volume Resistivity | 1.0e+15 | ohm.m | ASTM D 257 |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 9.5 / * | % | Sim. to ISO 62 |
| Humidity absorption | 2.8 / * | % | Sim. to ISO 62 |