To catalogue
Tarnoform® 300 AR
Tarnoform® 300 AR is a polyacetal copolymer (pom) polymer lowered wear and friction coefficient modified with aramid fibers.
Properties
- Physical Form
- Granules
- Solid
Product families
Plastics — Engineering & Specialty Polymers
- Polyacetals
Other characteristics
- Brand
- Tarnoform
- Polymer Name
- Polyacetal Copolymer (POM)
- Fillers Included
- Aramid, Aramid Fiber
- Aramid
- Aramid Fiber
- Flexural Modulus
- 3000.0 - 3000.0 MPa
- Processing Methods
- Injection Molding
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- Medium Viscosity
- Wear Resistant
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 65 | MPa | ASTM D638 |
| Tensile Modulus | 3100 | MPa | ASTM D 638 |
| Strain at break | 12 | % | ISO 527 |
| Flexural modulus, 23° | 3000 | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 5.5 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 50 | kJ/m2 | ISO 179/1eU |
| Izod notched impact strength, +23° | 5 | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 145 | MPa | ISO 2039-1 |
Table 2 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index - MFI (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D 1238 |
| Melt Mass Flow Rate - MFR (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Melt Volume Flow Rate - MVR (190°C/2.16 kg) | 2.2 | cm3/10 min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 1 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 5/- | % | ISO 294-4 |
| Molding shrinkage - parallel | 1.5 | % | ISO 294-4, 2577 |
| Density | 1410 | kg/m3 | ASTM D 792 |
Table 3 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Delfection Temperature Under Load (1.8 MPa) | 120 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 120 | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 167 | °C | ISO 11357-1-3 |
| Vicat Softening Temperature (50 N) | 140 | °C | ISO 306 |
| Melting temperature (10°C/min) | 167 | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 | mm | — |
| Vicat softening temperature | 140 | °C | ISO 306 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |