Tarnamid® T- 27 MHLS
- Chemical Family
- Polyamides
Tarnamid® T- 27 MHLS is a polyamide 6 UV stabilized to improve resistance against weathering influence.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Other Building Materials
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Tarnamid
- Polymer Name
- Polyamide 6 (PA 6)
- Additives Included
- UV Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- Good Weather Stability
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Construction Applications
- Electrical/Electronic Applications
- Household Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 100 | cm3/10min | ISO 1133 |
| Melt Volume Flow Rate - MVR (275°C/5 kg) | 100 / * | cm3/10 min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 1 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 6/1 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 8 | % | ISO 294-4 |
| Molding shrinkage - normal | 1.8 / * | % | ISO 294-4, 2577 |
| Molding shrinkage - parallel | 1.6 / * | % | ISO 294-4, 2577 |
| Water Absorption (23/sat.) | 9.5 | % | ISO 62 |
| Moisture Absorption (23°C/50% RH) | 3 | % | ISO 62 |
| Density | 1140 / - | kg/m3 | ISO 1183 |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Ball indentation hardness | 150 / 75 | MPa | ISO 2039-1 |
Table 3 of 5
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (parallel) | 90 / * | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 120 / * | E-6/K | ISO 11359-1/-2 |
| Delfection Temperature Under Load (1.8 MPa) | 60 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 60 / * | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 221 | °C | ISO 11357-1 |
| Vicat Softening Temperature (50 N) | 195 | °C | ISO 306 |
| Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
| Thickness tested | 1.6 / * | mm | — |
| Vicat softening temperature | 195 / * | °C | ISO 306 |
| Burning Behavior at 1.5 mm nominal thickness | HB / * | class | IEC 60695-11-10 |
| Burning Behavior at thickness | HB / * | class | IEC 60695-11-10 |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index - CTI | 600 | V | UL 746 |
| Surface Resistivity | 1.0e+15 | ohm | STN 34 6460 |
| Volume Resistivity | 1.0e+15 | ohm.m | ASTM D 257 |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 9.5 / * | % | Sim. to ISO 62 |
| Humidity absorption | 3 / * | % | Sim. to ISO 62 |