Tarnoform® 300 HI2
Grade with increased impact strength ISO 9988-1: POM-K, M-GNPR, 03-001
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
- Powertrain & UTH
- Seating
Automotive & Transportation — Bonding & Assembly
- Other Bonding & Assembly Applications
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Product Families
Plastics — Engineering & Specialty Polymers
- Polyacetals
Other characteristics
- Brand
- Tarnoform
- Polymer Name
- Polyacetal Copolymer (POM)
- Flexural Modulus
- 1750.0 - 1750.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- Impact Resistance
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Fasteners
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Mass Flow Rate - MFR (190°C/2.16 kg) | 9 | g/10 min | ASTM D1238 |
| Melt Flow Index - MFI (190°C/2.16 kg) | 9 | g/10 min | ASTM D 1238 |
| Melt Volume Flow Rate - MVR (190°C/2.16 kg) | 7.5 | cm3/10 min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 1 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 9/- | % | ISO 294-4 |
| Molding shrinkage - parallel | 1.9 | % | ISO 294-4, 2577 |
| Moisture Absorption (23°C/50% RH) | 0.3 | % | ISO 62 |
| Density | 1380 | kg/m3 | ASTM D 792 |
Table 2 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527 |
| Yield stress | 50 | MPa | ISO 527 |
| Yield strain | 12 | % | ISO 527 |
| Strain at break | 50 | % | ISO 527 |
| Flexural modulus, 23° | 1750 | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 12 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 250 | kJ/m2 | ISO 179/1eU |
| Izod notched impact strength, +23° | 12 | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 100 | MPa | ISO 2039-1 |
Table 3 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (parallel) | 130 | E-6/K | ISO 11359-1/-2 |
| Delfection Temperature Under Load (1.8 MPa) | 95 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 95 | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 167 | °C | ISO 11357-1-3 |
| Vicat Softening Temperature (50 N) | 130 | °C | ISO 306 |
| Melting temperature (10°C/min) | 167 | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 | mm | — |
| Vicat softening temperature | 130 | °C | ISO 306 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index - CTI | 600 | V | UL 746 |
| Surface Resistivity | 1.00E+13 | ohm | IEC 60093 |
| Volume Resistivity | 10000000000000.0 | ohm.m | IEC 60093 |
Table 5 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Humidity absorption | 0.3 | % | Sim. to ISO 62 |