Tarnamid® T-27 W
- Chemical Family
- Polyamides
Polyamide 6 specially UV-stabilized grades for outdoor applications. ISO 1874-1: PA 6, MHLR, 14-030
Properties
- Physical Form
- Granules
- Solid
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Tarnamid
- Polymer Name
- Polyamide 6 (PA 6)
- Processing Methods
- Injection Molding
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Certifications and Compliance
- UL 94
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 75 / - | MPa | ISO 527 |
| Tensile Modulus | 2500 / - | MPa | ISO 527 |
| Charpy notched impact strength (+23°) | 6 / - | kJ/m2 | ISO 179/1eA |
| Ball indentation hardness | 145 / - | MPa | ISO 2039-1 |
Table 2 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 80 | cm3/10min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 1 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 6/1 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 8 | % | ISO 294-4 |
| Water Absorption (23/sat.) | 9.5 | % | ISO 62 |
| Moisture Absorption (23°C/50% RH) | 3 | % | ISO 62 |
| Density | 1.14 | g/cm3 | ISO 1183/A |
Table 3 of 4
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Delfection Temperature Under Load (1.8 MPa) | 60 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 55 / * | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 221 | °C | ISO 11357-1 |
| Vicat Softening Temperature (50 N) | 195 | °C | ISO 306 |
| Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
| Vicat softening temperature | 175 / * | °C | ISO 306 |
Table 4 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability - Glow Wire Test | 650 | °C | IEC-60695-2-12 |