Tarnoform® 300 G2
Grade with lowered wear and friction coefficient modified with UHMWPE ISO 9988-1: POM-K, M-GNS2, 02-002
Properties
- Physical Form
- Granules
- Solid
Product families
Plastics — Engineering & Specialty Polymers
- Polyacetals
Other characteristics
- Brand
- Tarnoform
- Polymer Name
- Polyacetal Copolymer (POM)
- Flexural Modulus
- 2000.0 - 2000.0 MPa
- Processing Methods
- Injection Molding
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- Tribological Modified
- Wear Resistant
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index - MFI (190°C/2.16 kg) | 7 | g/10 min | ASTM D 1238 |
| Melt Mass Flow Rate - MFR (190°C/2.16 kg) | 7 | g/10 min | ASTM D1238 |
| Melt Volume Flow Rate - MVR (190°C/2.16 kg) | 6.5 | cm3/10 min | ISO 1133 |
| Density | 1330 | kg/m3 | ASTM D 792 |
Table 2 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527 |
| Yield stress | 45 | MPa | ISO 527 |
| Yield strain | 10 | % | ISO 527 |
| Strain at break | 15 | % | ISO 527 |
| Flexural modulus, 23° | 2000 | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 2 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 40 | kJ/m2 | ISO 179/1eU |
| Izod notched impact strength, +23° | 2 | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 105 | MPa | ISO 2039-1 |
Table 3 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Delfection Temperature Under Load (1.8 MPa) | 90 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 90 | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 167 | °C | ISO 11357-1-3 |
| Vicat Softening Temperature (50 N) | 135 | °C | ISO 306 |
| Melting temperature (10°C/min) | 167 | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 | mm | — |
| Vicat softening temperature | 135 | °C | ISO 306 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |