Braskem America CP360H
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Braskem CP360H polypropylene homopolymer is a high melt flow rate homopolymer designed for spunbond nonwoven production. This resin features an excellent processability allowing increased line speed or air pressure as well as gains of mechanical properties. The narrow molecular weight distribution AGF stability and tight gel control provide its unique performance.\nAll Braskem America production facilities are certified to produce bio, bio-circular, and circular polypropylene under the ISCC PLUS certification via the mass balance approach.\nFor more information regarding REACH, please visit Braskem's REACH site
Properties
- Physical Form
- Granules
- Pellets
- Solid
Product families
Applications
Industrial — Leather & Textiles
- Textile Manufacturing
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 34.0 g/10 min
- Processing Methods
Extrusion, Fibers Extrusion, High-speed Fiber Spinning, Injection Molding, Spunbond Nonwovens
- Markets
- Industrial
- Technology
- Plastics
- Key Attributes
- Narrow molecular weight distribution
- Low smoke/condensate
- Labeling Claims
- APE-free
- Animal Products-free
- Azo Colorants-free
- Azo Dyes-free
- Bio-attributed
- Bio-circular
- Biocides-free
- Bisphenol A-free
- Quality Standards
- GMP
- Material Features
- AGF Stability
- Food Contact Acceptable
- Good Mechanical Properties
- Good Processability
- Low Condensate
- Low Smoke Emission
- Narrow Molecular Weight Distribution
- No Added PFAS
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- EINECS (EU)
- ELINCS (EU)
- ENCS (Japan)
- IECSC (China)
- KECI (Korea)
- NZIoC (New Zealand)
Technical data
Table 1 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Yield (2 in/min, 50 mm/min) | 11 | % | ASTM D-638 |
| Tensile Strength at Yield (2 in/min, 50 mm/min) | 4,700 | psi | ASTM D-638 |
| Notched Izod Impact Strength (at 23°C) | 21 | J/m | D 256 |
| Rockwell Hardness (R Scale) | 100 | — | D 785 |
| Flexural Modulus (0.05 in/min, 1.3 mm/min, 1% secant) | 170,000 | psi | ASTM D-790A |
| Tenacity of Fibers (3.3 Draw Ratio 1250 M/Min Roll Speed 225°C Spin Temperature D1000/68) | 2.3 | g/denier | ASTM D-2256 |
| Elongation Of Fibers (3.3 Draw Ratio 1250 M/Min Roll Speed 225°C Spin Temperature D1000/68) | 117 | % | ASTM D-2256 |
| Suggested Takeup Roll Speed | 13,122 | ft/min | — |
Table 2 of 2
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Nominal Melt Flow (230°C/2.16kg) | min. 34 | g/10 | ASTM D-1238 |