SLD4004
- Chemical Family
- PolyethylenesPolyolefins
SLD4004 is a low-density polyethylene (LDPE) known for its excellent processability and good mechanical properties. This versatile resin can be utilized in various processing methods, including blow molding, compression molding, extrusion, and foam extrusion. With its low carbon content, SLD4004 aligns with sustainable practices, making it an eco-friendly choice. It excels in producing high-quality films and sheets, offering superior performance as a resin for plastics and elastomers.\nFor more information regarding REACH, please visit Braskem's REACH site
Product families
- Polyolefins
Other characteristics
- Brand
- I'm green bio-based
- Polymer Name
- Low Density Polyethylene (LDPE)
- Melt Flow Index
- 2.0 g/10 min
- Processing Methods
Blow Molding, Blown Film Extrusion, Compression Molding, Extrusion, Extrusion Blow Molding (EBM), Film Extrusion, Foam Extrusion
- Note
Typical Properties - Plaque Properties:. Test specimens from compression molded plaque according to ASTM D4703. Plaque Thickness: a) 2mm. b) 3mm c) 6mm. NB = No break
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Low Carbon Footprint (PCF)
- Sustainable
- Sustainable Polyethylene
- Quality Standards
- In Preview
- Material Features
- Good Mechanical Properties
- Good Processability
- Low Carbon Content
- Plastics and Elastomers End Uses
- Film
- Sheets
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blow Molding
- Blown Film Extrusion
- Compression Molding
- Extrusion
- Extrusion Blow Molding (EBM)
- Film Extrusion
- Foam Extrusion
Technical data
Table 1 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 190°C, 2.16kg) | 2.0 | g/10 min | ASTM D 1238 |
| Density | 0.923 | g/cm³ | ASTM D 792 |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength (at Break) ᵃ | 13.0 | MPa | ASTM D 638 |
| Elongation (at Break) ᵃ | 920.0 | % | ASTM D 638 |
| Flexural Modulus (1% Secant) ᵇ | 240.0 | MPa | ASTM D 790 |
| Hardness ᶜ | 45.0 | — | ASTM D 2240 |
| Vicat Softening Temperature (at 10 N) ᵇ | 92.0 | °C | ASTM D 1525 |
| Melting Temperature | 110.0 | °C | ASTM D 3417/D 3418 |