SLL5405S
- Chemical Family
- PolyethylenesPolyolefins
SLL5405S is a LLDPE Butene copolymer designed and produced by Braskem. This versatile product offers a great balance between processing performance, mechanical properties, and sealability. It exhibits very low gel amount, ensuring high-quality results. The minimum biobased carbon content of this grade is 87%, determined according to ASTM D6866.\nFor more information regarding REACH, please visit Braskem's REACH site
Product families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- I'm green bio-based
- Polymer Name
- Linear Low Density Polyethylene (LLDPE)
- Melt Flow Index
- 1.0 g/10 min
- Additives Included
- Anti-Blocking Agent, Slip Agent
- Anti-Blocking Agent
- Slip Agent
- Processing Methods
- Blown Film Extrusion, Extrusion, Film Extrusion
- Note
Blown Film Properties:; Film with 38 microns produce in a 40mm extruder and a blow‐up ratio of 2.2:1. (MD = extrusion direction and TD = transversal direction).
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Low Carbon Footprint (PCF)
- Sustainable
- Sustainable Polyethylene
- Quality Standards
- In Preview
- Material Features
- Excellent Performance
- Excellent Sealability
- Good Mechanical Properties
- Good Processability
- Low Carbon Content
- Low Gel
- Certifications and Compliance
- EC No.1907/2006
- Plastics and Elastomers End Uses
- Film
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blown Film Extrusion
- Extrusion
- Film Extrusion
Technical data
Table 1 of 2
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength (at Break, MD) | 40.0 | MPa | ASTM D882 |
| Tensile Strength (at Break, TD) | 30.0 | MPa | ASTM D882 |
| Elongation (at Break, MD) | 1070.0 | % | ASTM D882 |
| Elongation (at Break, TD) | 1340.0 | % | ASTM D882 |
| Tensile Modulus (1% Secant, MD) | 210.0 | MPa | ASTM D882 |
| Tensile Modulus (1% Secant, TD) | 230.0 | MPa | ASTM D882 |
| Dart Drop Impact Strength | 130.0 | g/F50 | ASTM D1709 |
| Elmendorf Tear Strength (MD) | 180.0 | gF | ASTM D1922 |
| Elmendorf Tear Strength (TD) | 400.0 | gF | ASTM D1922 |
Table 2 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 190°C, 2.16kg) | 1.0 | g/10 min | ASTM D1238 |
| Density | 0.918 | g/cm³ | ASTM D 792 |