SVT2180
- Chemical Family
- Vinyls Vinylics & Vinyl Derivatives
Braskem America SVT2180 is a copolymer of renewable ethylene with Vinyl Acetate (EVA) mainly used for the production of crosslinked foam sheets and other parts. It is a product with easy processability and high compatibility with mineral fillers, thermoplastics, and elastomeric resins. Other important characteristics are elasticity, flexibility, excellent stress cracking resistance (ESCR), chemical resistance, and low temperature strength. The exclusive morphologic characteristics give outstanding crosslinkability. The components produced with SVT2180 have the following properties: low weight, resistance to deformation, low shrinkage, high capacity of shrinkage, and color retention. The minimum biobased carbon content of this grade is 80%, determined according to ASTM D6866.
Properties
- Physical Form
- Granules
- Pellets
- Solid
Product families
- Vinyl Polymers
Other characteristics
- Brand
- I'm green bio-based
- End Uses
Foams, Midsole, Plates, Shoe Sole, Sporting Goods, Toys, Unisole
- Polymer Name
- Ethylene Vinyl Acetate Copolymer (EVA)
- Melt Flow Index
- 2.1 g/10 min
- Additives Included
- Antioxidant
- Processing Methods
- Compression Molding, Injection Molding
- Note
Typical Properties - Plaque Properties:; Test specimens prepared from compression molded plate according to ASTM D 4703.; Compression molded 2 mm thickness, 0.3 mm notched‐plaques; 100% Igepal; 50ºC.
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Footwear
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Bio-based
- Carbon Black-free
- Dye Free
- Pigment-free
- Recyclable
- Sustainable
- Quality Standards
- Astm D6866
- In Preview
- Material Features
Chemical Resistant; Crosslinkable; Excellent Compatibility; Excellent Elasticity; Good Environmental Stress Crack Resistance (ESCR); Good Flexibility; Good Processability; Light Weight; Low Deformation Tendency; Low Shrinkage; Low Temperature Strength; Renewable Resource Content
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- EINECS (EU)
- ENCS (Japan)
- IECSC (China)
- ISHL (Japan)
- KECI (Korea)
- NZIoC (New Zealand)
- Certifications and Compliance
ANVISA Resolution RDC No. 105/1999; ANVISA Resolution RDC No. 326/2019; ANVISA Resolution RDC No. 56/2012; ANVISA Resolution RDC No. 91/2001; Comprehensive Environmental Response Compensations & Liability Act (CERCLA); Directive 1333/2008/EC; EC No. 2023/2006; EC No.1907/2006; MERCOSUR Resolution GMC No. 02/12; MERCOSUR Resolution GMC No. 03/92; MERCOSUR Resolution GMC No. 39/19; MERCOSUR Resolution GMC No. 56/92; Regulation (EC) No. 1334/2008; Regulation (EU) No. 10/2011 (PIM); Regulation (EU) No. 1935/2004; Regulation (EU) No. 2023/1627; SARA 313
- Plastics and Elastomers End Uses
- Foams
- Midsole
- Plates
- Shoe Sole
- Sporting Goods
- Toys
- Unisole
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Compression Molding
- Injection Molding
Technical data
Table 1 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| C14 Content | min. 80 | % | ASTM D 6866 |
Table 2 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 190°C, 2.16kg) | 2.1 | g/10 min | ASTM D 1238 |
| Vinyl-Acetate Content | 19.0 | % | ASTM-D-5594-98 |
Table 3 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 0.94 | g/cm³ | ASTM D1505 / ASTM D792 |
| Tensile Strength (at Break) | 19.0 | MPa | ASTM D638 |
| Elongation (at Break) | 750.0 | % | ASTM D638 |
| 5% Secant Modulus | 33.0 | MPa | ASTM D638 |
| Hardness | 89.0 | Shore A | ASTM D2240 |
| Hardness | 38.0 | Shore D | ASTM D2240 |
| Melting Point | 86.0 | °C | ASTM D3418 |
| Vicat Softening Temperature (at 10 N) | 61.0 | °C | ASTM D1525 |