SGF4960
- Chemical Family
- PolyethylenesPolyolefins
SGF4960 is a homopolymer high-density polyethylene designed for the blow-molding segment. This product offers a winning combination of high density, stiffness, and exceptional impact resistance, making it ideal for various applications. With a minimum biobased carbon content of 96% (ASTM D6866), it demonstrates Braskem's commitment to sustainability. SGF4960's versatile properties make it well-suited for use in sports and recreation equipment, food and beverage packaging, and toys, among others. Its low carbon content further adds to its appeal as an eco-friendly choice.\nFor more information regarding REACH, please visit Braskem's REACH site
Product families
Applications
- Consumer Goods — Sports & Recreation
- Food & Beverage Packaging
- Non-Food Consumer Packaging
Product Families
- Polyolefins
Other characteristics
- Brand
- I'm green bio-based
- Polymer Name
High Density Polyethylene (HDPE), High Density Polyethylene (HDPE) Compound; High Density Polyethylene (HDPE); High Density Polyethylene (HDPE) Compound
- Melt Flow Index
- 28.0 g/10 min
- Processing Methods
Blow Molding, Compression Molding, Extrusion, Extrusion Blow Molding (EBM), Profile Extrusion, Tubing Extrusion
- Note
Typical properties correspond to average values obtained in our laboratories. Test specimens prepared from compression molded sheet made according to ASTM D 4703. Thickness of test piece: a) 2 mm; b) 3 mm.
- Markets
- Consumer Goods
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Low Carbon Footprint (PCF)
- Recyclable
- Sustainable
- Sustainable Polyethylene
- Quality Standards
- In Preview
- Material Features
- High Density
- High Impact Resistance
- High Stiffness
- Low Carbon Content
- Renewable Resource Content
- Chemical Inventories
- TSCA (USA)
- Certifications and Compliance
Comprehensive Environmental Response Compensations & Liability Act (CERCLA); SARA 313
- Plastics and Elastomers End Uses
- Beverage Bottles
- Bottles
- Caps
- Closures
- Containers
- Cosmetic Packaging
- Cosmetics Bottles
- Food Packaging
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blow Molding
- Compression Molding
- Extrusion
- Extrusion Blow Molding (EBM)
- Profile Extrusion
- Tubing Extrusion
Technical data
Table 1 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| C14 Content | min. 96 | % | ASTM D 6866 |
Table 2 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 190°C, 2.16kg) | 0.34 | g/10 min | ASTM D1238 |
| Density | 0.962 | g/cm³ | ASTM D792 |
Table 3 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 190°C, 21.6kg) | 28.0 | g/10 min | ASTM D 1238 |
| Tensile Strength (at Yield) ᵃ | 30.0 | MPa | ASTM D 638 |
| Tensile Strength (at Break) ᵃ | 30.0 | MPa | ASTM D 638 |
| Flexural Modulus (1% Secant) ᵇ | 1550.0 | MPa | ASTM D 790 |
| Tensile Impact Strength (at 23°C) | 90.0 | kJ/m² | ISO 8256 |
| Deflection Temperature Under Load (at 0.455 MPa) ᵇ | 70.0 | °C | ASTM D 648 |
| Vicat Softening Temperature (at 10 N) ᵇ | 132.0 | °C | ASTM D 1525 |