- Chemical Family
- PolyethylenesPolyolefins
SHC7260LS-L is a high-density polyethylene specially developed for injection molding applications. It offers high hardness and stiffness while exhibiting a low tendency to warp. This resin contains additives to protect against the damaging effects of ultraviolet radiation. With a minimum biobased carbon content of 94%, determined by ASTM D6866, this grade aligns with sustainable practices.\nFor more information regarding REACH, please visit Braskem's REACH site
Properties
- Physical Form
- Granules
- Pellets
- Solid
Product families
- Polyolefins
Other characteristics
- Brand
- I'm green bio-based
- Polymer Name
High Density Polyethylene (HDPE), High Density Polyethylene (HDPE) Compound; High Density Polyethylene (HDPE); High Density Polyethylene (HDPE) Compound
- Melt Flow Index
- 7.2 g/10 min
- Processing Methods
- Compression Molding, Injection Molding
- Note
Typical Properties - Plaque Properties:. Test specimens from compression molded plaque according to ASTM D4703. Plaque Thickness: a) 2mm. b) 3mm c) 6mm. NB = No break
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Low Carbon Footprint (PCF)
- Sustainable
- Sustainable Polyethylene
- Quality Standards
- In Preview
- Material Features
- Good Stiffness
- High Hardness
- Low Carbon Content
- Low Warpage
- UV Resistant
- Chemical Inventories
- DSL (Canada)
- TSCA (USA)
- Certifications and Compliance
Comprehensive Environmental Response Compensations & Liability Act (CERCLA)
- Plastics and Elastomers End Uses
- Crates
- Pallets
- Safety Helmets
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Compression Molding
- Injection Molding
Technical data
Table 1 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 190°C, 2.16kg) | 7.2 | g/10 min | ASTM D1238 |
| Density | 0.959 | g/cm³ | ASTM D792 |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength (at Yield) ᵃ | 29.0 | MPa | ASTM D638 |
| Elongation (at Yield) ᵃ | 7.5 | % | ASTM D638 |
| Flexural Modulus (1% Secant) ᵇ | 1375.0 | MPa | ASTM D2240 |
| Shore D Hardness ᶜ | 63.0 | — | ASTM D2240 |
| Izod Impact Strength ᵇ | 35.0 | J/m | ASTM D256 |
| Deflection Temperature Under Load (at 0.455 MPa) ᵇ | 74.0 | °C | ASTM D648 |
| Vicat Softening Temperature (at 10 N) ᵇ | 126.0 | °C | ASTM D1525 |