To catalogue
SLL318
- Chemical Family
- PolyethylenesPolyolefins
SLL318 is a linear low density polyethylene, copolymer of butene-1, developed specifically for cast film extrusion applications. Films produced with this product exhibit excellent mechanical properties and enhanced sealability. With a minimum biobased carbon content of 87%, as determined by ASTM D6866, this grade aligns with sustainable practices. Additionally, it contains oxidant additives to further enhance its performance.\nFor more information regarding REACH, please visit Braskem's REACH site
Properties
- Physical Form
- Pellets
Product families
Applications
Electrical & Electronics — Wire & Cable
- Jacketing & Insulation
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- I'm green bio-based
- Polymer Name
- Linear Low Density Polyethylene (LLDPE)
- Melt Flow Index
- 2.7 g/10 min
- Additives Included
- Antioxidant
- Processing Methods
- Cast Film Extrusion, Extrusion, Film Extrusion
- Note
Blown Film Properties:; Film with 38 microns produce in a 40mm extruder and a blow‐up ratio of 2.2:1. (MD = extrusion direction and TD = transversal direction).
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Low Carbon Footprint (PCF)
- Sustainable
- Sustainable Polyethylene
- Quality Standards
- In Preview
- Material Features
- Excellent Sealability
- Good Mechanical Properties
- Low Carbon Content
- Certifications and Compliance
- EC No.1907/2006
- Compatible Polymers and Resins
- High-Density Polyethylene (HDPE)
- Low-Density Polyethylene (LDPE)
- Polyethylene Cross-Linked (PEX)
- Plastics and Elastomers End Uses
- Electrical Insulation
- Film
- Liners
- Pipes
- Stretch Films
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Cast Film Extrusion
- Extrusion
- Film Extrusion
Technical data
Table 1 of 2
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength (at Break, MD) | 30.0 | MPa | ASTM D882 |
| Tensile Strength (at Break, TD) | 30.0 | MPa | ASTM D882 |
| Elongation (at Break, MD) | 1220.0 | % | ASTM D882 |
| Elongation (at Break, TD) | 1440.0 | % | ASTM D882 |
| Tensile Modulus (1% Secant, MD) | 180.0 | MPa | ASTM D882 |
| Tensile Modulus (1% Secant, TD) | 200.0 | MPa | ASTM D882 |
| Dart Drop Impact Strength | 90.0 | g/F50 | ASTM D1709 |
| Elmendorf Tear Strength (MD) | 120.0 | gF | ASTM D1922 |
| Elmendorf Tear Strength (TD) | 340.0 | gF | ASTM D1922 |
Table 2 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 190°C, 2.16kg) | 2.7 | g/10 min | ASTM D1238 |
| Density | 0.918 | g/cm³ | ASTM D1505 |