SHD7255LS-L is a high-density polyethylene specially designed for injection molding applications. It offers a combination of good tenacity, impact properties, and stiffness. The resin's unique ratio between melt flow and density contributes to excellent mechanical properties. Additionally, this product contains additives that protect against the action of ultraviolet radiation. With a minimum biobased carbon content of 94%, determined according to ASTM D6866, it is an environmentally friendly choice for various molding needs.\nFor more information regarding REACH, please visit Braskem's REACH site
Properties
- Physical Form
- Granules
- Pellets
- Solid
Product families
- Polyolefins
Other characteristics
- Brand
- I'm green bio-based
- Polymer Name
High Density Polyethylene (HDPE), High Density Polyethylene (HDPE) Compound; High Density Polyethylene (HDPE); High Density Polyethylene (HDPE) Compound
- Melt Flow Index
- 4.5 g/10 min
- Processing Methods
- Compression Molding, Injection Molding
- Note
Typical Properties - Plaque Properties:. Test specimens from compression molded plaque according to ASTM D4703. Plaque Thickness: a) 2mm. b) 3mm c) 6mm. NB = No break
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Low Carbon Footprint (PCF)
- Sustainable
- Sustainable Polyethylene
- Quality Standards
- In Preview
- Material Features
- Excellent Melt Flow
- Good Impact Strength
- Good Mechanical Properties
- Good Stiffness
- Good Tenacity
- Low Carbon Content
- UV Resistant
- Chemical Inventories
- DSL (Canada)
- TSCA (USA)
- Certifications and Compliance
Comprehensive Environmental Response Compensations & Liability Act (CERCLA)
- Plastics and Elastomers End Uses
- Boxes
- Crates
- Fish Crates
- Flip‐Top Caps
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Compression Molding
- Injection Molding
Technical data
Table 1 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 190°C, 2.16kg) | 4.5 | g/10 min | ASTM D1238 |
| Density | 0.954 | g/cm³ | ASTM D792 |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength (at Yield) ᵃ | 27.0 | MPa | ASTM D638 |
| Tensile Strength (at Break) ᵃ | 7.9 | MPa | ASTM D638 |
| Flexural Modulus (1% Secant) ᵇ | 1150.0 | MPa | ASTM D2240 |
| Shore D Hardness ᶜ | 60.0 | — | ASTM D2240 |
| Izod Impact Strength ᵇ | 45.0 | J/m | ASTM D256 |
| Deflection Temperature Under Load (at 0.455 MPa) ᵇ | 69.0 | °C | ASTM D648 |
| Vicat Softening Temperature (at 10 N) ᵇ | 124.0 | °C | ASTM D1525 |