Synergy Polymers RGR20FR
- Chemical Family
- Polyamides
Synergy Polymers RGR20FR is a Nylon 66 Flame Retardant VO Glass Filled 20%.
Product families
Applications
- Connectors
- Printed Circuit Boards (PCBs)
- Switches & Relays
- Terminal Blocks Plugs & Sockets
- Jacketing & Insulation
Product Families
- Polyamides
Other characteristics
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Additives Included
- Flame Retardant
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Features
Good mechancial & thermal properties, Warpage free moldings, dimensional stability, Resistance to creep and fatigue Resistance to arc-tracking. Meets UL94 VO rating.
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Material Features
- Creep Resistant
- Dimensional Stability
- Fatigue Resistant
- Flame Retardant
- Good Mechanical Properties
- Low Warpage
- Processing Guidelines
Synergy's Synlon (Nylon 6 & 66) is packed at maximum moisture content of 0.2% in moisture-proof, lined packaging. However Nylon being hygroscopic, it is advisable to dry the material at 100-120 degree centigrade for 2-4 hours. Natural and lighter shade material may be dried at lesser temp. and lesser duration to avoid discoloration, brittleness due to over heating. Then need for drying the material is evident by the formation of bubbles or foam in the melt, excessive drooling from the nozzle, or streaks in the molded parts.; Synergy's Synlon (Nylon 6 & 66) should be injected at fast injection speeds, to prevent premature crystallization. Low to medium injection pressures is recommended. Faster injection speeds and medium injection pressures provide a longer material flow path in the mold, better packing, good surface appearance, and low molded in stresses.; The Holding or packing pressure should be about 50 to 65% of the injection pressure. The holding pressure should be optimized to effectively control sink marks and flashing. Optimum extruder speed and back pressure must be used to ensure a uniform melt and shot size consistency. Sufficient back pressure ensures homegenous melt formation and elimination of gas voids in the melt. Use of shut-off nozzle is recommended to avoid drooling.; Conditioning : It is advised to condition in hot water at 80-100 Deg. C for 2-4 hrs. depending upon the component thickness and as required by the subsequent process also to release internal stresses if any to avoid breakage druing further assembly.
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Electronic Insulation
- Printed Circuit Boards
- Terminal Blocks
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding