HTC™ 9510
- Chemical Family
- Polyimides (PI)
HTC™ 9510 is an E-Glass Fiber reinforced Bismaleimide (BMI) ESC® molding compound. It exhibits outstanding elevated temperature characteristics providing greatly extended service temperature range versus epoxy compounds for compression molding applications.
Properties
- Physical Form
- Sheets
Product families
Applications
- Pipes & Plumbing
- Equipment & Parts
- Refining & Gas Processing
- Aerospace & Aviation
- Marine
Product Families
- Sheet Molding Compounds (SMC)
Other characteristics
- Brand
- HTC
- End Uses
- Tanks
- Functions
- Molding Compound
- Processing Methods
- Compression Molding
- Reinforcement Material
- Glass Fibers
- Color
- Black
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (10°F or below)
- Precaution
HTC™ 9510 contains glass fibers and should be handled carefully in order to minimize skin contact. Molding areas should be well ventilated to minimize exposure to fumes. Presses must be provided with local exhaust to remove vapors from work areas. If adequate ventilation is not available, a respirator approved for removing organic vapor must be used.
- Technology
- Composite Materials
- Packaging Type
- Rolls
- Composites End Use
- Tanks
- Material Features
- Good Mechanical Properties
- Temperature Resistance
- Molding Suggestions
HTC™ 9510 can be molded at temperatures in the range of 260-350° F, with 300° F suggested as a starting point. Cure times will be dependent on molding temperature and part thickness and will typically be 25+ minutes. Detailed molding suggestions are available on request. Cool molded parts at ambient temperature. A cooling fixture may be needed depending on part thickness and geometry.
- Compatible Polymers and Resins
- Polyimides (PI)
- Composite Materials Functions
- Molding Compound
- Composites Processing Methods
- Compression Molding
Technical data
Table 1 of 2
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.82 | g/cc | ASTM D-792 |
| Molding Shrinkage | 0.0015 (0.038) | inch/inch (mm/mm) | ASTM D-955 |
| Flexural Strength | 94,000 (648) | psi (MPa) | ASTM D-790 |
| Flexural Modulus | 4.0 x106 (27.6) | psi (GPa) | ASTM D-790 |
| Flexural Strength at 350° F | 70,000 (483) | psi (MPa) | ASTM D-790 |
| Tensile Strength | 28,500 (196) | psi (MPa) | ASTM D-638 |
| Tensile Modulus | 4.0 X106 (27.6) | psi (GPa) | ASTM D-638 |
| Tensile Strength at 350° F | 28,500 (196) | psi (MPa) | ASTM D-638 |
| Izod Impact (notched) (Net Shape) | 30 (1600) | ft.lb./in. (J/M) | ASTM D-256 |
| Compressive | 36,000 (248) | psi (MPa) | ASTM D-3410 |
| Compressive at 350° F | 32,000 (221) | psi (MPa) | ASTM D-3410 |
| Glass Transition Temperature | 700 (371) | °F (°C) Tan Delta | ASTM D-7028 |
Table 2 of 2
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Carbon Fiber Content (Nominal) | -52 | % w/w |
| Resin Content (Nominal) | -48 | % w/w |
| Fiber Length (Nominal) | 1 | inch |