ARCOR® EE-121
ARCOR® EE-121 is a solvent-free, high 3.6 functionality epoxy Novolac coating specifically engineered for both immersion and non-immersion service. Unlike traditional Epoxy Novolac Resin based coatings, this advanced formulation is designed to excel in aggressive chemical environments and withstand elevated temperatures. ARCOR® EE-121 is specifically tailored to handle tough chemical environments, including acids, methanol, ethanol, and organic solvents. By integrating Kevlar® fibers, it creates a robust, highly cross-linked coating that exhibits exceptional chemical resistance, flexural strength, thermal stability, impact resistance, and wear resistance. This versatile coating is suitable for use on ferrous and nonferrous metals as well as concrete, making it a reliable choice for both immersion and non-immersion containment applications. Choose ARCOR® EE-121 for superior protection and performance in demanding chemical environments, ensuring long-lasting durability and resistance to various corrosive substances. ARCOR Epoxy Technologies can tailor make or reformulate the product to suit customer needs. Please reach out if you need a custom formulated product!
Identification
Product families
Applications
- Equipment & Parts
Product Families
- Top Coats
Other characteristics
- Brand
- ARCOR
- Features
Acid Resistant, Alkali Resistant, Chemical Resistant, Excellent Solvent Resistance, Good Abrasion Resistance, Good Flexibility, Good Toughness, High Temperature Resistance, Water Resistant
- Product Type
Epoxy Coating, Solventless & High Solids Coating, Top Coat; Epoxy Coating; Solventless & High Solids Coating; Top Coat
- Application Area
Floor, Flue Gas Desulfurization (FGD), Pipes, Pump, Tank Lining; Floor; Flue Gas Desulfurization (FGD); Pipes; Pump; Tank Lining
- Application Method
- Brush, Roller, Spray
- Mixing
Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade scraping sides and bottom of container or mixing board. Mix by Volume 2-parts Base to 1-part Activator. Or by weight 100 grams Base to 50 grams Activator. Mix thoroughly to produce an even colored and streak-free material.
- Markets
- Industrial
- Clean Up
Clean tools immediately after use with M.E.K., Acetone, 98+% Isopropyl Alcohol or similar
- Mix Ratio
2:1 by Volume (Base : Activator) 100 gm : 50 gm by weight
- Shelf LIfe
- 5 Years (at 13-35ºC)
- Application
Brush: medium to stiff bristle of sufficient quality that bristles do not pull out and stick in coating. Trim or tape to <1" nap. Roller: good quality 1/8" nap. Plural Spray: 0.029-0.031 tip, 3,000-3,500 PSI, Heat to 130ºF Base, 110ºF Activator. Airless Spray: Not Recommended Conventional Spray: Not Recommended All spray equipment should employ traps to prevent water and oil from contaminating coating and screens to prevent particulate contamination.
- Cure
- Chemical Cure
- Flexibility
Good; Very Good with Polyester or Fiberglass Mat; 1.5 oz/ft2 (.5 KG/M2)
- Technology
- Ready-to-Use Products
- Film Thickness
- 20-60 mils (.51- 1.53 mm)/coat
- Labeling Claims
- Solvent-free
- Weight per Gallon
- 10.7 lbs. (4.9 KG)
- 2.8 lbs. (1.3 KG)/Liter
- Application Methods
- Brush
- Roller
- Spray
- Overcoat and Cure Time
By brush, roller or squeegee recoat while material is still soft, but tack-free, between 1-3 hours at 77ºF(25ºC).
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Maximum Temperature for Immersion Service | 177.0 | °C |
| Temperature Spike Tolerance for Immersion Service (3hrs) | 232.0 | °C |
| Recommended Force Cure Temperature (2hrs) | 121.0 | °C |
| Maximum Temperature for Dry Heat | 260.0 | °C |
| Temperature Spike Tolerance for Dry Heat | 304.0 | °C |
Table 2 of 2
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 100.0 | % Volume |
| Viscosity | 120,000-180,000 | cps |
| Pot Life (at 72°F) | 15.0 | min/100gr |
| Coverage | 26-80 | ft² / gal / coat |