ARCOR® Spraythane
- Chemical Family
- Epoxy & Epoxy Derivatives
ARCOR® Spraythane is a high elongation, elastomeric, hybridized epoxy/urethane coating. It offers exceptional resilience, tear resistance, and impact resistance, making it an excellent choice for combating cavitation and abrasion. This versatile coating is fully compatible with epoxy coatings. The combination of epoxy and urethane in ARCOR® Spraythane provides a durable and flexible resilience, along with improved water and chemical resistance. It also boasts excellent shelf stability. Unlike traditional urethanes, ARCOR® Spraythane's epoxy reactivity eliminates moisture sensitivity and toxicity concerns. This coating delivers a smooth finish and effortlessly self-levels in horizontal applications. ARCOR Epoxy Technologies can tailor make or reformulate the product to suit customer needs. Please reach out if you need a custom formulated product!
Product families
Applications
- Other Flooring & Surface Applications
Product Families
- Top Coats
Other characteristics
- Brand
- ARCOR
- Features
Abrasion Resistant, Acid Resistant, Alkali Resistant, Cavitation Protection, Chemical Resistant, Good Flexibility, Good Toughness, High Elongation, High Impact Resistance, High Resilience, Improved Tear Strength, Water Resistant
- Product Type
Elastomeric Coating, Epoxy Coating, Solventless & High Solids Coating, Top Coat; Elastomeric Coating; Epoxy Coating; Solventless & High Solids Coating; Top Coat
- Application Area
- Decking, Manways
- Decking
- Manways
- Application Method
- Brush, Roller, Spray
- Compatible Substrates & Surfaces
- Concrete
- Mixing
Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade, thoroughly scrape sides and bottom. Mix by volume 2 part Base to 1 part activator. Or by weight 100 gm Base to 52 gm activator. Mix thoroughly to produce and even colored, streak-free material.
- Markets
- Building & Construction
- Clean Up
Clean tools immediately after use with M.E.K., Acetone, 98+% Isopropyl Alcohol or similar
- Mix Ratio
2:1 by Volume (Base:Activator) 100 gm: 52 gm by Weight
- Application
All spray equipment should employ traps to prevent water and oil from contaminating coating and screens to prevent particulate contamination.
- Cure
- Chemical Cure
- Flexibility
- Excellent; Elongation 300%
- Technology
- Ready-to-Use Products
- Film Thickness
- 20 mils(.51 mm)/coat Immersion 1-2 coats.
- Weight per Gallon
- 10.8 lbs (4.89 KG)
- Application Methods
- Brush
- Roller
- Spray
- Overcoat and Cure Time
Recoat between 6 and 12 hours at 77ºF (25ºC).; Full cure before immersion 72 hours at 77ºF. Force Cure: 12 hours at 120ºF (49ºC).
- Ready to Use Product Features
- Abrasion Resistant
- Acid Resistant
- Alkali Resistant
- Cavitation Protection
- Chemical Resistant
- Good Flexibility
- Good Toughness
- High Elongation
- Compatible Substrates and Surfaces
- Concrete
Technical data
Table 1 of 2
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Maximum Temperature for Immersion Service | 66.0 | °C |
| Temperature Spike Tolerance for Immersion Service (3hrs) | 82.0 | °C |
| Maximum Temperature for Dry Heat | 163.0 | °C |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 100.0 | — | — |
| Pot Life (at 72°F) | 55.0 | min/gal | — |
| Coverage | 80.0 | ft² / gal / coat | Theoretical |
| Hardness | 80.0 | Shore A | — |
| Impact Resistance Direct | 400.0 | in-lbs | — |
| Viscosity | 60,000-90,000 | cps | — |