ARCOR® EE-111
ARCOR® EE-111 is a solvent-free, high 3.6 functionality epoxy Novolac coating specifically designed for immersion and non-immersion service in aggressive chemical environments with elevated temperatures and high abrasion. This versatile coating creates a tough and chemically resistant protective layer on ferrous and non-ferrous metals as well as concrete surfaces. With the incorporation of micro ceramic spheres, ARCOR® EE-111 offers exceptional abrasion resistance while still allowing for plural spray application, making it suitable for large-scale projects. Its low viscosity and 3.6 functionality epoxy Novolac composition enable easy application by hand or spray, with a recommended thickness of up to 25 mils per coat. This coating can withstand immersion temperatures of up to 350ºF (162ºC). Notably, ARCOR® EE-111 exhibits excellent resistance to various aggressive chemicals such as Methanol, Glacial Acetic Acid, Methylene Chloride, Hydrochloric Acid, Nitric Acid, and Sulphuric Acid. ARCOR Epoxy Technologies can tailor make or reformulate the product to suit customer needs. Please reach out if you need a custom formulated product!
Identification
Product families
Applications
- Equipment & Parts
Product Families
- Top Coats
Other characteristics
- Brand
- ARCOR
- Features
Acid Resistant, Alkali Resistant, Chemical Resistant, Excellent Solvent Resistance, Good Abrasion Resistance, Good Flexibility, Good Toughness, High Temperature Resistance, Low Viscosity, Water Resistant
- Product Type
Epoxy Coating, Solventless & High Solids Coating, Top Coat; Epoxy Coating; Solventless & High Solids Coating; Top Coat
- Application Area
Flue Gas Desulfurization (FGD), Induced Draught Fan (ID Fan) , Scrubber, Tank Lining; Flue Gas Desulfurization (FGD); Induced Draught Fan (ID Fan); Scrubber; Tank Lining
- Application Method
- Brush, Roller, Spray
- Compatible Substrates & Surfaces
- Concrete, Metal
- Mixing
Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade scraping sides and bottom of container or mixing board. Mix by Volume 2 parts Base to 1 part Activator. Or by weight 100 grams base to 60 grams activator. Mix thoroughly to produce an even colored and streak-free material.
- Markets
- Industrial
- Clean Up
Clean tools immediately after use with M.E.K., Acetone, 98+% Isopropyl Alcohol or similar
- Mix Ratio
2:1 by Volume (Base:Activator) 100 gm: 60 gm by weight
- Shelf LIfe
- 5 Years (at 13-35ºC)
- Application
Brush: medium to stiff bristle of sufficient quality that bristles do not pull out and stick in coating. Trim or tape to <1" nap. Roller: good quality 1/8"-1/4" nap. Plural Spray: 0.5290-.531 tip, 2,500-3,500 PSI, Heat to 150ºF Base, 150ºF Activator, Line Heat @ 190ºF, Hose Heat @ 150ºF. Use 30 mesh screens, 2-3 in-line static mixers. Keep additional material in hotbox @ 120-140ºF. Airless Spray: Not Recommended Conventional Spray: Not Recommended All spray equipment should employ traps to prevent water and oil from contaminating coating
- Cure
- Chemical Cure
- Flexibility
Very Good Excellent with Polyester Mat; 1.5 oz/ft² (5. KG/M²)
- Technology
- Ready-to-Use Products
- Film Thickness
20-80 mils(.51-2.04 mm)/coat Splash: 1-2 coats, Immersion: 1-2 coats (up to 80 mils in one coat)
- Labeling Claims
- Solvent-free
- Weight per Gallon
- 12 lbs (5.44 KG)
- Application Methods
- Brush
- Roller
- Spray
Technical data
Table 1 of 2
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Maximum Temperature for Immersion Service | 177.0 | °C |
| Temperature Spike Tolerance for Immersion Service (With force cure at 250ºF, 6 Hrs) | 204.0 | °C |
Table 2 of 2
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Coverage | 20-80 | ft² / gal / coat |
| Solid Content | 100.0 | % Volume |
| Viscosity | 35,000-50,000 | cps |
| Pot Life (at 72°F) | 15.0 | min/150gr |