ARCOR® EE-951 HT
ARCOR® EE-951 HT is a solvent-free, high 3.6 functionality epoxy Novolac that serves as an exceptional rebuilding material for metals in highly aggressive chemical and temperature immersion service. Designed with precision, ARCOR® EE-951 HT is an ideal choice for restoration or cladding purposes, providing superior corrosion and abrasion protection. With its remarkable application flexibility, ARCOR® EE-951 HT can be applied up to an impressive 500 mils without any concerns of slump. Experience the reliability and performance of ARCOR® EE-951 HT, delivering outstanding protection and durability for your metal surfaces in the most demanding and challenging environments. ARCOR Epoxy Technologies can tailor make or reformulate the product to suit customer needs. Please reach out if you need a custom formulated product!
Identification
Product families
Applications
- Industrial — Maintenance
- Repair & Overhaul
- Equipment & Parts
Product Families
- Other Construction Chemicals
Other characteristics
- Brand
- ARCOR
- Features
Acid Resistant, Alkali Resistant, Chemical Resistant, Corrosion Resistant, Excellent Solvent Resistance, Good Abrasion Resistance, Good Flexibility, High Temperature Resistance
- Product Type
Bonding Putty, Epoxy Adhesive, Repair Material, Solvent free (100% Solids) Adhesive; Bonding Putty; Epoxy Adhesive; Repair Material; Solvent free (100% Solids) Adhesive
- Application Area
- Filters, Tank Lining
- Filters
- Tank Lining
- Application Method
- Air Knife Coating, Wipe
- Mixing
Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade scraping sides and bottom of container or mixing board. Mix by Volume 3 parts Base to 1 part Activator. Mix thoroughly to produce an even colored, streak-free material.
- Markets
- Industrial
- Clean Up
Clean tools immediately after use with M.E.K., Acetone, 98+% Isopropyl Alcohol or similar
- Mix Ratio
3:1 by Volume (Base : Activator) 100 gm: 33 gm by Weight
- Shelf LIfe
- 5 Years (at 13-35ºC)
- Flexibility
Very Good Excellent with Polyester Mat; 1.5 oz/ft² (5. KG/M²)
- Technology
- Ready-to-Use Products
- Film Thickness
- Good Fair Flexural Strength 12,000 psi
- Weight per Gallon
- 12.1 lbs (5.6 KG)
- Application Methods
- Air Knife Coating
- Wipe
- Surface Preparation
Steel surfaces are to be abrasive blasted with chloride free abrasive. Exterior applications to SSPC SP-10 Near White metal finish. Immersion applications to SSPC SP-5 White metal 3 to 5 mil profile. Grind flat all burrs, weld seams, radius sharp edges. Fresh blasted ferrous surfaces to be primed immediately with ARCOR™ S-30 Prime or ARCOR™ EE- 101 to prevent oxidation of surface. Concrete surfaces should be degreased if oil and grease contamination is present. Degreased surface shall be high pressure washed, acid etched and high pressure washed again so surface is clean and free of all grease, oils and surface laitance. Existing coatings should be abrasive blasted to clean concrete. Prime with ARCOR™ EE-101, EE-111.. Concrete surfaces should be degreased if oil and grease contamination is present. Degreased surface shall be high pres- sure washed, acid etched and high pressure washed again so surface is clean and free of all grease, oils and surface laitance. Existing coatings should be abrasive blasted to clean concrete. Prime with ARCOR™ EE-101.
- Ready to Use Product Features
- Acid Resistant
- Alkali Resistant
- Chemical Resistant
- Corrosion Resistant
- Excellent Solvent Resistance
- Good Abrasion Resistance
- Good Flexibility
- High Temperature Resistance
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Maximum Temperature for Immersion Service | 191.0 | °C |
| Temperature Spike Tolerance for Immersion Service (3hrs) | 246.0 | °C |
| Recommended Force Cure Temperature (2hrs) | 79.0 | °C |
| Recommended Force Cure Temperature (3hrs) | 149.0 | °C |
| Maximum Temperature for Dry Heat | 260.0 | °C |
| Temperature Spike Tolerance for Dry Heat (3hrs) | 304.0 | °C |
Table 2 of 2
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 100.0 | % Volume |
| Pot Life (at 72°F) | 25.0 | min/kg |