ARCOR® Spraythane FL
- Chemical Family
- Epoxy & Epoxy Derivatives
ARCOR® Spraythane FL is a high elongation, elastomeric, hybridized epoxy/urethane coating. It offers exceptional resilience, tear resistance, and impact resistance, making it an excellent choice for combatting cavitation and abrasion. This versatile coating is fully compatible with epoxy coatings. The urethane aspect of ARCOR® Spraythane FL delivers a tough and flexible resilience, while the epoxy aspect provides improved water and chemical resistance, as well as shelf stability. Notably, the epoxy reactivity of this product eliminates the moisture sensitivity and toxicity commonly associated with traditional urethanes. ARCOR® Spraythane FL is a reliable and durable solution for a wide range of coating applications. ARCOR Epoxy Technologies can tailor make or reformulate the product to suit customer needs. Please reach out if you need a custom formulated product!
Product families
Applications
- Other Flooring & Surface Applications
Product Families
- Top Coats
Other characteristics
- Brand
- ARCOR
- Features
Abrasion Resistant, Acid Resistant, Alkali Resistant, Cavitation Protection, Chemical Resistant, Good Flexibility, Good Toughness, High Elongation, High Impact Resistance, High Resilience, Improved Tear Strength, Water Resistant
- Product Type
Elastomeric Coating, Epoxy Coating, Solventless & High Solids Coating, Top Coat; Elastomeric Coating; Epoxy Coating; Solventless & High Solids Coating; Top Coat
- Application Area
- Concrete Flooring, Decking, Manways
- Concrete Flooring
- Decking
- Manways
- Application Method
- Brush, Roller, Spray
- Compatible Substrates & Surfaces
- Concrete
- Mixing
Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade, thoroughly scrape sides and bot- tom. Mix by volume 2 part Base to 1 part activator, by weight 100 gm Base to 52.2 gm activator.
- Markets
- Building & Construction
- Clean Up
Clean tools immediately after use with M.E.K., Acetone, 98+% Isopropyl Alcohol or similar
- Mix Ratio
2:1 by Volume (Base:Activator) 100 gm: 52.2 gm by Weight
- Shelf LIfe
- 5 Years (at 13-35ºC)
- Application
All spray equipment should employ traps to prevent water and oil from contaminating coating and screens to prevent particulate contamination.
- Cure
- Chemical Cure
- Flexibility
- Excellent Elongation 300%
- Technology
- Ready-to-Use Products
- Film Thickness
- 20 mils(.51 mm)/coat Immersion 1-2 coats.
- Application Methods
- Brush
- Roller
- Spray
- Surface Preparation
Concrete surfaces should be degreased if oil and grease contamination is present. Degreased surface shall be high pressure washed, acid etched and high pressure washed again so surface is clean and free of all grease and oils and surface laitance. Existing coatings should be abrasive blasted to clean concrete. Prime with ARCOR™ EE-70, EE-79 or ARCOR™ EE-10.
- Overcoat and Cure Time
Recoat between 6 and 12 hours at 77ºF (25ºC).; Full cure before immersion 72 hours at 77ºF. Force Cure: 12 hours at 120ºF (49ºC).
- Ready to Use Product Features
- Abrasion Resistant
- Acid Resistant
- Alkali Resistant
- Cavitation Protection
- Chemical Resistant
- Good Flexibility
- Good Toughness
- High Elongation
- Compatible Substrates and Surfaces
- Concrete
Technical data
Table 1 of 2
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Maximum Temperature for Immersion Service | 66.0 | °C |
| Temperature Spike Tolerance for Immersion Service (3hrs) | 82.0 | °C |
Table 2 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coverage | 27-80 | ft² / gal / coat | Theoretical |
| Solid Content | 1.0 | — | — |
| Viscosity | 90,000-130,000 | cps | — |
| Pot Life (at 72°F) | 55.0 | min/gal | — |