Bioblend LT25B R
- Chemical Family
- PolyestersPolylactic Acid (PLA)
Bioblend LT25B R are developed for rigid injection molded applications. The grades can be crystallized/annealed in order to have the part heat-stable at temperatures up to 110°C. Bioblend LT grades are biodegradable in controlled conditions.
Properties
- Physical Form
- Solid
Product families
- Biodegradable Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- Bioblend
- Density
- 1300.0 - 1300.0 kg/m³
- Polymer Name
- Polylactic Acid (PLA)
- Labeling Claims
Bio-based, Biodegradable, Food Contact Acceptable, Low Carbon Footprint (PCF); Bio-based; Biodegradable; Food Contact Acceptable; Low Carbon Footprint (PCF)
- Fillers Included
Coffee Husk, Natural Fiber, Rice Husk, Wheat Husk; Coffee Husk; Natural Fiber; Rice Husk; Wheat Husk
- Processing Methods
- Injection Molding
- Drying
Dry the material for a minimum of 4 - 6 hours at 80o C. A moisture content of less than 0.07% (700 ppm) is required / less than 0.10% (1000 ppm) is recommended. Avoid exposing the material to atmospheric conditions after drying; process immediately.
- Markets
- Consumer Goods
- Personal Care
- Printing & Packaging
- Storage
Keep the material tightly closed in a dry and cool place. Keep away from heat and sources of ignition and avoid exposure to moisture, dampness. Do not stor outdoors. Use material within 6 month after delivery.
- Technology
- Plastics
- Material Features
- Biodegradable
- Compostable
- Easier Processing
- Excellent Stiffness
- Excellent Strength
- Flexible
- Food Contact Acceptable
- Good Elongation
- Process Guidelines
Bioblend LT25B (B/R/C/W/H) can be processed on conventional injection molding equipment. The material is sensitive to moisture and high temperatures (above 190°C); high shear rates shall be avoided. The matrial needs to be dried before processing. Do not keep the material in the heated barrel longer than 5 – 8 minutes; the material is prone to degrade.
Technical data
Table 1 of 2
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.3 | g/cm3 | — |
| Melt Flow Rate (190°C/2.16 kg) | min. 70.0 | g/10 min | ASTM D1238 |
| HDT-B (0.46 MPa) | 54.2 | °C | ASTM D648 |
| Tensile Strength (50 mm/min) | 51.7 | Mpa | ASTM D638 |
| Flexural Strength | 65.2 | Mpa | ASTM D790A |
| Flexural Modulus (1% secant) | 5.3 | Gpa | ASTM D790A |
| Elongation at Yield (50 mm/min) | 7.5 | % | ASTM D638 |
| Elongation at Break (50 mm/min) | 31 | % | ASTM D638 |
| IZOD Notched Impact Strength (at 23°C) | 31.5 | J/m | ASTM D256 |
| Mold Shrinkage | 0.45 | % | — |
| Density (annealing, 5 minutes at 130°C) | 1.3 | g/cm3 | — |
| HDT-B (0.46 Mpa, annealing, 5 minutes at 130°C) | min. 125.0 | °C | ASTM D648 |
Table 2 of 2
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Hopper Temperature | Room Temperature | — |
| Feed Zone Temperature | 180 | °C |
| Compression Zone Temperature | 185 | °C |
| Metering Zone Temperature | 190 | °C |
| Nozzle Temperature | 185 | °C |
| Mould Temperature | 50-60 | °C |
| Screw Speed | Low – Medium | — |
| Injection Pressure | Low | — |
| Holding Pressure | Long | — |
| Injection Speed | Slow | — |
| Cooling Time | Long | — |