Nylene® PX3422
- Chemical Family
- Polyamides
Nylene Heat stabilized, high impact modified nylon resin designed for maximum toughness with minimum sacrifice in tensile strength and melting point Offers outstanding elongation and good retention of that elongation after 5 days of heat aging at 177°C (95% elongation) Optimum processing conditions should provide a melt temperature of 490 - 530°F at the die Suitable for processing in either extrusion or injection molding applications
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Nylene
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 1450.0 - 1450.0 MPa
- Additives Included
- Heat Stabilizer, Impact Modifier
- Heat Stabilizer
- Impact Modifier
- Processing Methods
- Extrusion, Injection Molding
- Technology
- Plastics
- Material Features
- Good Toughness
- Heat Aging Resistant
- Heat Stabilized
- Impact Modified
- Country Availability
- Canada
- USA
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 45 | MPa | ASTM D638 |
| Elongation at Break | 310 | % | ASTM D 638 |
| Flexural Modulus | 1450 | MPa | ASTM D 790 |
| Izod Notched Impact Strength (23°C) | 1070 | J/m | ASTM D256 |
Table 2 of 3
1 row| Characteristic | Value | Method |
|---|---|---|
| Specific Gravity | 1.07 | ASTM D 792 |
Table 3 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Deflection Temperature Under Load - DTUL (1.82 MPa) | 42 | °C | ASTM D648 |
| Melting Point | 214 | °C | ASTM D3418 |