GRANOC YARN YSH-60A
- Chemical Family
- Carbon Fiber
GRANOC YARN YSH-60A is a high compressive strength for aerospace application.
Properties
- Physical Form
- Fabric
Product families
Applications
Applications
- Consumer Goods — Sports & Recreation
Automotive & Transportation — Automotive
- Powertrain & UTH
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Composite Materials — Reinforcements
- Carbon Fiber
Other characteristics
- Brand
- GRANOC YARN
- Features
Ease of Handling, Easy Handling, Excellent Elasticity, Good Processability, Good Thermal Conductivity, Good Thermal Stability, High Modulus of Elasticity, High Performance, High Stiffness, Light Weight, Lightweight, Low Thermal Expansion, Thermal Stability
- Reinforcement Form
- Woven Fabric
- Reinforcement Material
- Carbon Fibers
- Markets
- Automotive & Transportation
- Consumer Goods
- Technology
- Composite Materials
- Composites End Use
- Driveshafts
- Microwave Antennas
- Material Features
- Ease of Handling
- Excellent Elasticity
- Good Processability
- Good Thermal Conductivity
- Good Thermal Stability
- High Performance
- High Stiffness
- Light Weight
- Composite Materials Functions
- Reinforcement
Technical data
Table 1 of 2
22 rows| Characteristic | Value | Unit |
|---|---|---|
| Tensile Strength | 560 | ksi |
| Tensile Strength | 390 | kgf/mm2 |
| Tensile Strength | 3830 | MPa |
| Tensile Strength | 560.0 | ksi |
| Tensile Strength | 390.0 | kgf/mm2 |
| Tensile Strength | 3830.0 | MPa |
| Tensile Modulus | 92 | msi |
| Tensile Modulus | 64.5 | 103kgf/mm2 |
| Tensile Modulus | 630 | GPa |
| Tensile Modulus | 92.0 | msi |
| Tensile Modulus | 630.0 | GPa |
| Ultimate Elongation | 0.6 | % |
Table 2 of 2
14 rows| Characteristic | Value | Unit |
|---|---|---|
| 0 deg Tensile Strength | 2150 | MPa |
| 0 deg Tensile Strength | 2150.0 | MPa |
| 0 deg Tensile Modulus | 380 | GPa |
| 0 deg Tensile Modulus | 380.0 | GPa |
| Elongation | 0.5 | % |
| 0 deg Compressive Strength | 490 | MPa |
| 0 deg Compressive Strength | 490.0 | MPa |
| 0 deg Compressive Modulus | 350 | GPa |
| 0 deg Compressive Modulus | 350.0 | GPa |
| 90 deg Tensile Strength | 37 | MPa |
| 90 deg Tensile Strength | 37.0 | MPa |
| 90 deg Tensile Modulus | 6.5 | GPa |