Wonderlite® PC-108
- Chemical Family
- Polycarbonate (PC)
Properties
- Physical Form
- Pellets
- Powder
Product families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- Wonderlite
- Polymer Name
- Polycarbonate (PC)
- Flexural Modulus
- 2400.0 - 2400.0 MPa
- Processing Methods
- Injection Molding
- Color
- Natural
- Markets
- Consumer Goods
- Applications
Consumer Goods — Other Consumer Goods Applications
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- General Purpose
- Country Availability
- China (Mainland)
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- General Purpose
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield | 61.8 | MPa | ASTM D 638 |
| Elongation at Yield | 6 | % | ASTM D 638 |
| Elongation at Break | 110 | % | ASTM D 638 |
| Stress at break | 75 | MPa | ISO 527 |
| Yield stress | 65 | MPa | ISO 527 |
| Flexural Strength | 90.3 | MPa | ASTM D790 |
| Flexural modulus, 23° | 2400 | MPa | ISO 178 |
| Flexural Modulus | 2355 | MPa | ASTM D 790 |
| Charpy notched impact strength (+23°) | 75 | kJ/m2 | ISO 179/1eA |
| Izod notched impact strength, +23° | 80 | kJ/m2 | ISO 180/1A |
| Izod Impact notched (1/8 in) | 848 | J/m | ASTM D 256 |
| Izod Impact notched (1/4 in) | 135 | J/m | ASTM D 256 |
Table 2 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index - MFI (300°C/1.2 kg) | 6.5 | g/10 min | ASTM D 1238 |
| Melt Volume Flow Rate - MVR (300°C/1.2 kg) | 6.5 | cm3/10 min | ISO 1133 |
| Mold Shrinkage (MD) | 0.006 | mm/mm | ASTM D 955 |
| Mold Shrinkage (TD) | 0.006 | mm/mm | ASTM D 955 |
| Density | 1200 | kg/m3 | ISO 1183 |
Table 3 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (MD) | 70 | E-6/K | ASTM D 696 |
| Deflection Temperature Under Load (66 psi) | 136 | °C | ASTM D 648 |
| Deflection Temperature Under Load (264 psi) | 125 | °C | ASTM D 648 |
| Temperature of deflection under load (1.80 Mpa) | 128 | °C | ISO 75-1/-2 |
| Thermal Conductivity of solid | 0.2 | W/(m K) | ASTM C 177 |
| Thickness tested | 1.5 | mm | — |
| Vicat softening temperature | 145 | °C | ISO 306 |
| Vicat Temperature | 148 | °C | ASTM D 1525 |
Table 4 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dissipation Factor (1 MHz) | 0.009 | — | ASTM D 150 |
| Dissipation Factor (60 Hz) | 0.0004 | — | ASTM D 150 |
| Dielectric Strength (Short Time) | 30 | kV/mm | ASTM D 149 |
| Dielectric Constant (60 Hz) | 2.95 | — | ASTM D 150 |
| Dielectric Constant (1 MHz) | 2.9 | — | ASTM D 150 |
| Arc Resistance | 110 | s | ASTM D 495 |
| Volume Resistivity | min. 1E15 | ohm.m | ASTM D 257 |
Table 5 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Haze | 0.8 | % | ASTM D 1003 |
| Index of Refraction | 1.58 | — | ASTM D 542 |
| Light Transmittance | 89 | % | ASTM D 1003 |
Table 6 of 7
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame rating | HB | UL 94 |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption (24 hr) | 0.2 | % | ASTM D 570 |