To catalogue
Polyrex® PH-88S
- Chemical Family
- High-Impact Polystyrene (HIPS)Styrenics
POLYREX® PH-88S is a High Impact Polystyrene product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America.Characteristics include: Flame Rated RoHS Compliant
Properties
- Physical Form
- Pellets
- Solid
Product families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- Polyrex
- Polymer Name
- High Impact Polystyrene (HIPS)
- Melt Flow Index
- 2.6 - 2.6 g/10 min
- Processing Methods
- Extrusion
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Cold-Chain & Insulation
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- Impact Resistance
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- RoHS Compliant
- UL 94
- Plastics and Elastomers End Uses
- Refrigeration
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 4
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 23.5 | MPa | ASTM D 638 |
| Stress at break | 24 | MPa | ISO 527 |
| Yield stress | 25 | MPa | ISO 527 |
| Flexural Strength | 35.2 | MPa | ASTM D790 |
| Flexural modulus, 23° | 1400 | MPa | ISO 178 |
| Flexural Modulus | 1793 | MPa | ASTM D 790 |
| Charpy notched impact strength (+23°) | 14 | kJ/m2 | ISO 179/1eA |
| Izod Impact notched (1/8 in) | 123 | J/m | ASTM D 256 |
| Izod notched impact strength, +23° | 13 | kJ/m2 | ISO 180/1A |
| Izod Impact notched (1/4 in) | 108 | J/m | ASTM D 256 |
| Ball indentation hardness | 76 | MPa | ISO 2039-1 |
| Rockwell Hardness | 75 | Scale L | ASTM D 785 |
Table 2 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index - MFI (200°C/0.5 kg) | 2.6 | g/10 min | ASTM D 1238 |
| Melt Volume Flow Rate - MVR (200°C/0.5 kg) | 3 | cm3/10 min | ISO 1133 |
| Density | 1050 | kg/m3 | ISO 1183 |
Table 3 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temperature of deflection under load (1.80 Mpa) | 77 | °C | ISO 75-1/-2 |
| Thickness tested | 1.5 | mm | — |
| Vicat Temperature | 100 | °C | ASTM D 1525 |
| Vicat softening temperature | 100 | °C | ISO 306 |
| Burning Behavior at 1.5 mm nominal thickness | HB | class | IEC 60695-11-10 |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame rating | HB | UL 94 |