Polyumac Stru-Cell Structural PVC P60
Polyumac Stru-Cell Structural PVC P60 is a high performance PVC foam core that sets the standard for sandwich composite structures. As well as its excellent strength to weight ratio, it offers good dimensional stability at elevated temperatures and its closed-cell construction means that it does not absorb water.
Properties
- Physical Form
- Sheets
Product families
Applications
Automotive & Transportation — Automotive
- Chassis & Brake
- Exterior & Body
- Interior
- Powertrain & UTH
Building & Construction — Building Materials
- Other Building Materials
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Power, Water & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Aerospace & Aviation
- Marine
- Rail & Mass Transit
Product Families
Composite Materials — Core Materials
- Foam Cores
Other characteristics
- Core Type
- Polyvinyl Chloride (PVC) Foam
- Functions
- Core Material
- Compatible Polymers & Resins
- Epoxies (EP), Polyesters, Vinyl Esters
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Core
- Polyvinyl Chloride (PVC) Foam
- Key Features
High strength to weight ratio; Excellent dimensional stability; Can be processed at up to 212° F (100° C); Good 'in service' temperature performance; Does not absorb water; Compatible with all the main resin systems (polyester, epoxy and vinylester systems).
- Technology
- Composite Materials
- Composites End Use
- Bulkheads
- Deck Panels
- Floors
- Hulls
- Wind Turbine Blades
- Material Features
- Dimensional Stability
- High Strength to Weight Ratio
- Chemical Inventories
- TSCA (USA)
- Compatible Polymers and Resins
- Epoxies (EP)
- Polyesters
- Vinyl Esters
- Composite Materials Functions
- Core Material
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Density | 4.1 (65) | lb/ft³ (kg/m³) |
| Tolerance | ±15 | % |
| Compressive Strength | 130 (0.9) | psi (Mpa) |
| Compressive Modulus | 9,860 (68) | psi (Mpa) |
| Shear Strength | 130 (0.9) | psi (Mpa) |
| Shear Modulus | 90 (22) | psi (Mpa) |
| Shear Elongation at Break | 20 | % |
| Tensile Strength | 261 (1.8) | psi (Mpa) |
| Tensile Modulus | 11,600 (80) | psi (Mpa) |