TRIFILON BIOLITE® 24
- CAS Number
- 9003-07-0
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Trifilon BioLite® 24 is a hemp fiber reinforced homopolymer for injection molding. It is designed for high stiffness and strength.
Product families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- TRIFILON BIOLITE
- Polymer Name
- Polypropylene (unspecified)
- Melt Flow Index
- 3.0 - 10.0 g/10 min
- Fillers Included
- Natural Fiber
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Attributes
Good Stiffness & Strength, Homopolymer, Biocomposite
- Availability
- Europe
- Technology
- Plastics
- Processing Method
- Injection Molding
- Material Features
- Good Stiffness
- Good Strength
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 2640 | MPa | ISO 527-2 |
| Tensile Stress at Break | 41 | — | — |
| Tensile Strain at Break | 4.5 | % | — |
| Charpy Impact Strength Unnotched at 20°C | 23 | kJ/m² | — |
| Charpy Impact Strength Notched (20°C) | 2.3 | kJ/m² | ISO 179/1eU |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1 | g/cm3 | ISO 1133 |
| Melt Flow Index - MFI | 3-10 | g/10 min | ISO 1133 |
| MFI Temperature | 230 | °C | — |
| MFI Load | 2.16 | kg | — |
Table 3 of 4
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Feeding Zone | 40 | °C |
| Zone 1 | 150 | °C |
| Zone 2 | 170 | °C |
| Zone 3 | 180 | °C |
| Zone 4 | 185 | °C |
| Machine Nozzle | 190 | °C |
| Mass Temperature | 190 | °C |
| Hot Runner | 190 | °C |
| Mould Temperature | 20-50 | °C |
Table 4 of 4
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Screw RPM | min. 10 | — |
| Back Pressure | 30-80 | bar |
| Shot Volume | 1-3 D | — |
| Max. Injection Pressure | min. 1000 | bar |
| Injection Speed | Low | — |
| Holding Pressure Level | 40-70 | % |
| Holding Pressure Time | 10-30 | sec |
| Melt Cushion (of volume) | 5-10 | % |
| Cooling Time | 10-50 | sec |