XTX Composites 3216FR Epoxy Resin
- Chemical Family
- Epoxy & Epoxy Derivatives
XTX Composites 3216FR Epoxy Resin is mainly applied in fire retardant level requirement of fiber reinforced composite material structures, such as rail transportation, yachts, car interiors and part structure composite material. This resin composite material structure, when heated and close to the fire will not release toxic and harmful gasses. Especially suitable for infusion process, RTM process (low viscosity and low surface tension of resin can quickly be capillary action, fully infiltrate various reinforced material) and had lay-up process. 3216FR resin with 3216AH is for infusion process; 3216FR resin with 3216BH is for hand lay-up process.
Product families
Applications
- Interior
- Structural Components
- Pavement Highways Roads & Bridges
- Rail & Mass Transit
Product Families
- Thermoset Resins
Other characteristics
- End Uses
- Structural Reinforcement
- Polymer Name
- Epoxy Resins & Compounds
- Processing Methods
Hand Lay-up, Resin Film Infusion (RFI), Resin Transfer Molding (RTM)
- Markets
- Automotive & Transportation
- Building & Construction
- Appearance
- No Obvious Impurity
- Technology
- Composite Materials
- Composites End Use
- Structural Reinforcement
- Material Features
- Flame Retardant
- Low Viscosity
- Curing Process
3216FR epoxy resin system can curing at high than 15℃，if need to get the best mechanical properties and thermal properties, must be conducted under the condition of temperature after curing. Recommended to curing at room temperature after exothermic peak, after the exothermic peak, temperature to 80℃，the curing after 10 hours. Concrete curing temperature, curing time and heating rate should be carried out according to the product structure adjustment, to ensure that products fully cured.
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Hand Lay-up
- Resin Film Infusion (RFI)
- Resin Transfer Molding (RTM)
- Typical Performance of Resin Casting
After exothermic peak at room temperature curing, curing at 80℃ by eight hours; 3216FR+3216AH; This date is the average data for the laboratory test data.
- Flame Retardant Performance Of Resin Casting
- 19.0 CFE(kW/m2)
- 102.4 MARHE(kW/m2)
- Concentration Of Harmful Gas After Combustion
Detection limit 0.2 mg/m³; NOX（use NO2 measuring）; NOTICE: The client should provide glass fiber reinforced plastics laminate with gel coat as roof facing material
- The Resin Blend System Technical Requirements
- 3216FR+3216AH
Technical data
Table 1 of 1
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Viscosity (25℃) | 900-1400 | mPa·s |
| Epoxy Equivalent | 188 | g/Eq |