INFINO GP-8200G
Product families
Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Pipes & Plumbing
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- INFINO
- Polymer Name
- Polyphenylene Ether (PPE)
- Fillers Included
- Glass Fiber
- Filler
- Glass Fiber
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Technology
- Plastics
- Material Features
- General Purpose
- Plastics and Elastomers End Uses
- Pump Parts
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.19 | — | ISO 1183 |
| Melt Flow Index - MFI (280°C/10 kg) | 7 | g/10 min | ISO 1133 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.42~0.52 | % | ISO 294-4 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.38~0.46 | % | ISO 294-4 |
Table 2 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (50 mm/min) | 120 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 120 | MPa | ISO 527 |
| Rockwell Hardness | 121 | Scale R | ISO 2039-2 |
| Tensile Modulus (50 mm/min) | 5500 | MPa | ASTM D 638 |
| Tensile Strain at Break (50 mm/min) | 3 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 170 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 5900 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 13 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 13 | kJ/m2 | ISO 180 1A |
Table 3 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 149 | °C | ISO 75-2 |