INFINO AR-5300H
- Chemical Family
- Polyesters
Product families
Applications
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
- Other Automotive Applications
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- INFINO
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Fiber
- Filler
- Glass Fiber
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Material Features
- General Purpose
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.45 | — | ISO 1183 |
| Melt Flow Index - MFI (250°C/5 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.1 - 0.4 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.2 - 0.5 | % | ISO 294-4 |
Table 2 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (50 mm/min) | 110 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 105 | MPa | ISO 527 |
| Rockwell Hardness | 117 | Scale R | ASTM D 785 |
| Tensile Modulus (50 mm/min) | 7000 | MPa | ISO 527 |
| Tensile Strain at Break (50 mm/min) | 5 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 170 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 7800 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 8 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 8 | kJ/m2 | ISO 180 1A |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 180 | °C | ISO 75-2 |
Table 4 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Ash Content | 30 | % | ASTM D4218 |