Starex LD-0955
- Chemical Family
- Acrylics Acrylates & Methacrylates
Product families
Plastics — Basic Thermoplastics
- Acrylates & Methacrylates
Other characteristics
- Brand
- Starex
- End Uses
- Appliances
- Polymer Name
- Polymethyl Methacrylate (PMMA)
- Melt Flow Index
- 22.0 - 22.0 g/10 min
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Appliances & Electronics
- Technology
- Plastics
- Material Features
- General Purpose
- Plastics and Elastomers End Uses
- Appliances
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (50 mm/min) | 55 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 45 | MPa | ISO 527 |
| Rockwell Hardness | 117 | Scale R | ASTM D 785 |
| Tensile Modulus (50 mm/min) | 2500 | MPa | ASTM D638 |
| Tensile Strain at Break (50 mm/min) | 10 | % | ISO 527-2/1A |
| Flexural Strength (2 mm/min) | 90 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2500 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 2 | kJ/m2 | ISO 179 1eA |
| Charpy Unnotched Impact Strength (23°C, 4mm) | 30 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 2 | kJ/m2 | ISO 180 1A |
| Unnotched Izod Impact Strength (23°C, 4 mm) | 25 | kJ/m2 | ISO 180 1A |
Table 2 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.17 | — | ISO 1183 |
| Melt Flow Index - MFI (220°C/10 kg) | 22 | g/10 min | ASTM D 1238 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.3 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.3 | % | ISO 294-4 |
Table 3 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 75 | °C | ISO 75-2 |