To catalogue
Starex WR-9700 T
- Chemical Family
- Styrenics
Product families
Applications
Building & Construction — Building Materials
- Pipes & Plumbing
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- Starex
- Polymer Name
- Acrylonitrile Styrene Acrylate (ASA)
- Melt Flow Index
- 11.0 - 11.0 g/10 min
- Processing Methods
- Extrusion
- Markets
- Building & Construction
- Technology
- Plastics
- Plastics and Elastomers End Uses
- Fittings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (50 mm/min) | 47 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 35 | MPa | ISO 527 |
| Rockwell Hardness | 109 | Scale R | ASTM D 785 |
| Tensile Modulus (50 mm/min) | 2200 | MPa | ASTM D 638 |
| Tensile Strain at Break (50 mm/min) | 15 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 67 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 1860 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 10 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 7 | kJ/m2 | ISO 180 1A |
Table 2 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.07 | — | ISO 1183 |
| Melt Flow Index - MFI (220°C/10 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.40~0.70 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.40~0.70 | % | ISO 294-4 |
Table 3 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 92 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 80 | °C | ISO 75-2 |