Starex GR-5035U
- Chemical Family
- Styrenics
Product families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- Starex
- Polymer Name
- Styrene Acrylonitrile Copolymer (SAN)
- Melt Flow Index
- 6.0 - 6.0 g/10 min
- Fillers Included
- Glass Fiber
- Filler
- Glass Fiber
- Markets
- Consumer Goods
- Applications
Consumer Goods — Other Consumer Goods Applications
- Technology
- Plastics
- Material Features
- General Purpose
- Plastics and Elastomers End Uses
- General Purpose
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.34 | — | ISO 1183 |
| Melt Flow Index - MFI (220°C/10 kg) | 6 | g/10 min | ISO 1133 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.5~0.6 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.5~0.6 | % | ISO 294-4 |
Table 2 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (50 mm/min) | 120 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 118 | MPa | ISO 527 |
| Rockwell Hardness | 123 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 9000 | MPa | ISO 527 |
| Tensile Strain at Break (50 mm/min) | 2 | % | ISO 527-2/1A |
| Flexural Strength (2 mm/min) | 180 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 11500 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 6 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 5.5 | kJ/m2 | ISO 180 1A |
Table 3 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 106 | °C | ISO 75-2 |