Starex LX-0915G
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
Product families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- Starex
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Melt Flow Index
- 17.0 - 17.0 g/10 min
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Appliances & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- General Purpose
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.15 | — | ISO 1183 |
| Melt Flow Index - MFI (220°C/10 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.1 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.1 | % | ISO 294-4 |
Table 2 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (5 mm/min) | 79 | MPa | ISO 527 |
| Tensile Strength at Break (5 mm/min) | 718 | MPa | ISO 527 |
| Rockwell Hardness | 112 | Scale R | ASTM D785 |
| Tensile Modulus (5 mm/min) | 6000 | MPa | ISO 527 |
| Tensile Strain at Break (5 mm/min) | 3 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 103 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 4810 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 7 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 6.5 | kJ/m2 | ISO 180 1A |
Table 3 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 100 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 97 | °C | ISO 75-2 |