INFINO SC-1060P
- Chemical Family
- Polycarbonate (PC)
Product families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- INFINO
- Polymer Name
- Polycarbonate (PC)
- Markets
- Consumer Goods
- Applications
Consumer Goods — Other Consumer Goods Applications
- Flame Rating
- UL 94 HB
- UL 94 V2
- Technology
- Plastics
- Material Features
- General Purpose
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- General Purpose
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.2 | — | ISO 1183 |
| Melt Flow Index - MFI (300°C/1.2 kg) | 6 | g/10 min | ASTM D 1238 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.5~0.7 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.5~0.7 | % | ISO 294-4 |
Table 2 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (50 mm/min) | 66 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 66 | MPa | ISO 527 |
| Rockwell Hardness | 120 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 2300 | MPa | ASTM D 638 |
| Tensile Strain at Break (50 mm/min) | 110 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 93 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2300 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 80 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 85 | kJ/m2 | ISO 180 1A |
Table 3 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 126 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 138 | °C | ISO 75-2 |
| Vicat Softening Temperature (B/50) | 147 | °C | ISO 306 |