To catalogue
Starex LX-0951
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
Product families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- Starex
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Melt Flow Index
- 29.0 - 29.0 g/10 min
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Appliances & Electronics
- Technology
- Plastics
- Material Features
- General Purpose
- Plastics and Elastomers End Uses
- Appliances
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (50 mm/min) | 50 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 40 | MPa | ISO 527 |
| Rockwell Hardness | 111 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 2500 | MPa | ASTM D638 |
| Tensile Strain at Break (50 mm/min) | 9.5 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 79 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2600 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 15 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 14 | kJ/m2 | ISO 180 1A |
Table 2 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.05 | — | ISO 1183 |
| Melt Flow Index - MFI (220°C/10 kg) | 29 | g/10 min | ISO 1133 |
| Melt Flow Index - MFI | 0.34~0.42 | g/10 min | ISO 1133 |
| Molding Shrinkage - MD | 0.35~0.43 | % | ISO 294-4 |
Table 3 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 90 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 77 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Annealed, 4 mm) | 95 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Annealed, 4 mm) | 99 | °C | ISO 75-2 |