Starex BF-0677HF
- Chemical Family
- Acrylics Acrylates & MethacrylatesStyrenics
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Other Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- Starex
- Polymer Name
Methyl Methacrylate Acrylonitrile Butadiene Styrene (MABS)
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Material Features
- General Purpose
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.13 | — | ISO 1183 |
| Melt Flow Index - MFI (220°C/10 kg) | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.4 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.5 | % | ISO 294-4 |
Table 2 of 3
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Break (50 mm/min) | 38 | MPa | ISO 527 |
| Tensile Strength at Yield (50 mm/min) | 53 | MPa | ISO 527 |
| Rockwell Hardness | 116 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 2600 | MPa | ASTM D638 |
| Tensile Strain at Break (50 mm/min) | 20 | % | ISO 527-2/1A |
| Flexural Strength (2 mm/min) | 80 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2600 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 10 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 10 | kJ/m2 | ISO 180 1A |
| Pencil Hardness (500 g) | H | — | JIS K 5401 |
Table 3 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 76 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 88 | °C | ISO 75-2 |
| Vicat Softening Temperature (B/50) | 95 | °C | ISO 306 |