Starex HF-1023IM
- Chemical Family
- Polycarbonate (PC)
Product families
Applications
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- Starex
- Polymer Name
- Polycarbonate (PC)
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- General Purpose
- Plastics and Elastomers End Uses
- Cell Phones
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (50 mm/min) | 60 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 96 | MPa | ISO 527 |
| Rockwell Hardness | 120 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 2100 | MPa | ASTM D638 |
| Tensile Strain at Break (50 mm/min) | 102 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 88 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2100 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 68 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 63 | kJ/m2 | ISO 180 1A |
Table 2 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.18 | — | ISO 1183 |
| Melt Flow Index - MFI (250°C/10 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.44~0.53 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.45~0.55 | % | ISO 294-4 |
Table 3 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 120 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 133 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Annealed, 4 mm) | 120 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Annealed, 4 mm) | 130 | °C | ISO 75-2 |