Starex VH-0815 M
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Other Devices & Assemblies
Electrical & Electronics — Wire & Cable
- Jacketing & Insulation
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- Starex
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Melt Flow Index
- 4.0 - 4.0 g/10 min
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 5VA
- UL 94 5VB
- UL 94 V0
- UL 94 V1
- UL 94 V2
- Technology
- Plastics
- Material Features
- Flame Retardant
- Certifications and Compliance
- RoHS Compliant
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Cables
- Electrical/Electronic Applications
- Wires
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (50 mm/min) | 46 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 34 | MPa | ISO 527 |
| Rockwell Hardness | 107.8 | Scale R | ISO 2039-2 |
| Tensile Modulus (50 mm/min) | 2269 | MPa | ISO 527 |
| Flexural Strength (2 mm/min) | 73 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 3483 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 20.4 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 18.6 | kJ/m2 | ISO 180 1A |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity (Natural or representative color) | 1.155 | — | ISO 1183 |
| Melt Flow Index - MFI (200°C/5 kg) | 4 | g/10 min | ASTM D 1238 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.31 - 0.59 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.31 - 0.59 | % | ISO 294-4 |
Table 3 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 86 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 70.4 | °C | ISO 75-2 |
| Vicat Softening Temperature (B/50) | 85.7 | °C | ISO 306 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (V-1) | 1.5 | mm | UL94 |
| Flammability (V-2) | BK 0.8 | mm | UL94 |