Crestaform® Open 3D printing resin
Crestaform® Open 3D printing resin is a versatile 3D printing resin designed for rapid prototyping and the creation of high-resolution models. It offers a fast and efficient method of fabrication. Compatible with various types of resin 3D printers, such as LCD, SLA, and DLP machines, it is suitable for use with popular brands including Formlabs, Asiga, Anycubic, and Elegoo.
Product families
- Photoactive Resins
Other characteristics
- Brand
- Crestaform
- Density
- 1,080.0 - 1,100.0 kg/m³
- End Uses
- Dental Applications, Jewelry, Prototyping
- Tensile Strength
- 69.0 MPa
- Processing Methods
3D Printing, Digital Light Processing, Masked Stereolithography (LCD), Stereolithography
- Note
Mechanical Testing Specimen Print Orientation - 50°; * 16 mins at 60°C + 405nm UV Post Cure for cured properties
- Markets
- Healthcare & Pharma
- Industrial
- Technology
- Plastics
- Colour Options
- Gray
- Color
- Grey
- Storage Condition
Crestaform® Open should be stored in the dark, in suitable, closed containers. It is recommended that the storage temperature should be between 15°C and 35°C. Ideally, containers should be opened only immediately prior to use. Keep out direct light/sunlight.
- Recommended Cleaning
Soak the print in a clean isopropanol (IPA) (or similar solvent) bath for a minimum of 5 minutes. Alternatively, rinse the part with IPA until all the visible uncured resin has been removed. Reusing IPA in multiple cleans can reduce the cleanliness and clarity of a print. Leave the print to dry off any residual solvent prior to post-curing
- Packaging Information
Crestaform® Open is supplied in 1000 g bottles. Bulk supply available.
- Recommended Post-Curing
Post-cure as soon as possible after completion of printing; Post-cure every print for a minimum of 10 minutes under a dedicated curing UV light operating at 405nm wavelength. Alternatively, leave the print to cure for a minimum of 2 hours under direct sunlight; Temperature-assisted UV curing will increase the rigidity of the print
- Plastics and Elastomers End Uses
- Dental Applications
- Jewelry
- Prototyping
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 2
2 rows| Characteristic | Value | Unit |
|---|---|---|
| ICI Viscosity (at 25°C) | 6.0 - 8.0 | Poise |
| Liquid Density | 1.08 - 1.10 | g/cm³ |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength* | 69.0 | MPa | ISO 527-2 Type 5A |
| Tensile Modulus* | 3.3 | GPa | ISO 527-2 Type 5A |
| Elongation (at break)* | 4.5 | % | ISO 527-2 Type 5A |
| Flexural Strength* | 111.0 | MPa | ISO 178 |
| Flexural Modulus* | 2.5 | GPa | ISO 178 |
| Hardness* | 83.0 | Shore D | ISO 868 |
| Heat Deflection Temperature (1.8 MPa)* | 55.0 | °C | ISO 75-2, Method A |