Plitek 8125 2 mil Blue EVA With Taffeta Finish
Properties
- Physical Form
- Film
Other characteristics
- Color
- Blue, Opaque
- Blue
- Opaque
- Density
- 930.0 - 930.0 kg/m³
- Features
- Matte Finish
- Polymer Name
- EVA/LDPE Alloy
- Shelf LIfe
- 1 Year from date of manufacture
- Technology
- Plastics
- Product Families
- Plastics — Parts, Shapes & Films
- Product Features
EVA/LDPE copolymer resin film with 8.7% vinyl acetate with thermal stabilizer; Finish: Taffeta/Matte; Film is self-wound
- Additives Included
- Thermal Stabilizer
- Material Features
- Matte Finish
- Technical information
Taffeta finish increases the original film thickness by almost 2 mil thickness. Original film thickness with matte finish is 2.0 +/- 0.3 mil.
- Certifications and Compliance
- ISO 13485
- ISO 9001
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Thickness (Taffeta Finish) | 3.7 +/- 0.3 | mil | PTM - QA - 005 |
| Thickness (Matte Finish) | 2.0 +/- 0.3 | mil | PTM - QA - 005 |
| Specific Gravity | 0.93 | g/cm³ | ASTM - D1505 |
| Gloss (at 60°) | 7.0 | GU | ASTM - D2457 |
| Transmittance | 18.0 | % | ASTM - E792 |
Table 2 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Elongation at Break (MD/TD) | 195/480 | % | ASTM - D882 |
| Tensile Strength at Break (MD/TD) | 3835/2360 | psi | ASTM - D882 |
Table 3 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature | 77.0 | °C | ASTM - D1525 |
| Melt Mass-Flow Rate (190 C/2.16kg) | 2.0 | g/10 min | ASTM - D1238 |
| Melting Temperature | 101.0 | °C | ISO-3146 |
| Peak Crystallization Temperature | 85.0 | °C | ASTM - D3418 |