TPV - ELASTRON V201.A41.N
A soft, colorable thermoplastic vulcanizate, TPV (EPDM/PP) in the thermoplastic elastomer (TPE) family which offers higher temperature resistance and excellent compression set with superior UV resistance.
Properties
- Physical Form
- Pellets
- Solid
Product families
- Thermoplastic Vulcanizates (TPV)
Other characteristics
- Brand
- TPV - ELASTRON
- Density
- 970.0 - 970.0 kg/m³
- Polymer Name
- Thermoplastic Vulcanizate (TPV)
- Tear Strength
- 15.0 - 15.0 kN/m
- Processing Methods
- Extrusion, Injection Molding
- Compression Set (70 °C)
- 24.0 - 24.0 %
- Color
- Natural
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Personal Care
- Printing & Packaging
- Appearance
- Colorable
- Technology
- Elastomers
- Features of Food
The monomers and additives used in manufacturing food contact TPE grades should be listed in the Union List of Authorized Substances of Regulation 10/2011/EC on plastic materials and articles intended to come into contact with food. Ingredients used in manufacturing these products are subject to a specific migration limit (SML). Elastron provides the quality and conditions of above mentioned regulation and limits. • Excellent bonding to many thermoplastics • Easy to color • Excellent surface appearance • Soft touch compounds • Availability of transparent grades • 100% recyclable • NSF 51/61 Compliant Grades
- Food Applications
With the help of the experiences gained from manufacturing of medical TPE compounds, Elastron offers high quality food contact TPE compounds. • Food Packing • Food Box Seals • Grips for Kitchen Equipments • Water Pump Seals
- Incompatible With
- PVC, Acetal
- Quality Standards
- ASTM International
- Material Features
- Acid Resistant
- Good Colorability
- Good Compression Set
- Good UV Resistance
- High Temperature Resistance
- Soft
- Soft Touch
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 100°C for 22 hr) | 28 | % | ASTM D 395 |
| Compression Set (at 23°C for 22 hr) | 16 | % | ASTM D 395 |
| Compression Set (at 70°C for 22 hr) | 24 | % | ASTM D 395 |
| Density | 0.97 | g/cm³ | ASTM D 792 |
| Durometer Hardness | 41 | Shore A | ASTM D 2240 |
| Elongation at Break | 600 | % | ASTM D 412 |
| Modulus of Elasticity (100%) | 1.2 | MPa | ASTM D 412 |
| Modulus of Elasticity (300%) | 2.1 | MPa | ASTM D 412 |
| Tear Resistance | 15 | N/mm | ASTM D 624 |
| Tensile Strength at Break | 3.5 | MPa | ASTM D 412 |
Table 2 of 6
1 row| Characteristic | Value |
|---|---|
| Ozone Resistance Stressed | No Cracks |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Across Flow | 1.86 | % | ASTM D 955 |
| Flow | 3.45 | % | ASTM D 955 |
Overview of the Chemical Resistance V201
4 rows| Characteristic | Value |
|---|---|
| Acid Bases Salts | Good Good Good |
| Aqeous Solutions Organic Solvents | Good Variable |
| Oils Automotive Oils | Swells Swells |
| Other Automotive Fluids | Good |
Physical and Chemical Effects of Fluids on Elastomers V201
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation at break | D412; die c | E |
| Tensile Strength | D412; die c | TS |
| Hardness | D2240 (3 sec. delay) | H |
| Weight Change | D471 | W |
| Volume Change | D471 | V |
Physical and Chemical Effects of Fluids on Elastomers V201
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| A | |<20| | Good | Very good suitability Elastomer shows little or no effect from exposure. Little effect on performance and physical properties. Very good resistance |
| B | |20 - 39| | Fair | Good suitability Some effects from exposure with some loss of physical properties Some chemical swelling |
| C | |40 - 59| | Not recom. | Limited suitability Significantly swell and loss of physical properties aſter exposure |
| D E F | |60 - 79| |80 - 100| |>100| | Not recom. Not recom. Not recom. | The elastomer is unsuitable for application in this media The elastomer is unsuitable for application in this media The elastomer is unsuitable for application in this media |