Polynil® P40/4

Chemical Family: Polyamides

Nilit POLYNIL® P40/4 is an unreiforced Polyamide 66 (Nylon 66) for compounding and alloying.This general pourpose 2.5 viscosity Polyamide 66 resin is FDA compliant.POLYNIL® P40/4 has moisture content lower than 0.4%.

Product families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: Polynil
Polymer Name: Polyamide 66 (PA 66)
Flexural Modulus: 2850.0 - 2850.0 MPa
Processing Methods: Compounding
Flame Rating: IEC 60695-11-10 V2
Technology: Plastics
Country Availability: Brazil
Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Compounding

Technical data

Table 1 of 4

10 rows

Characteristic	Value	Unit	Method
Tensile Modulus	3100	MPa	ASTM D 638
Yield stress	81	MPa	ISO 527
Strain at break	50	%	ISO 527
Flexural modulus, 23°	2850	MPa	ISO 178
Charpy impact strength (+23°)	N	kJ/m2	ISO 179/1eU
Charpy notched impact strength (+23°)	5.5	kJ/m2	ISO 179/1eA
Charpy notched impact strength (-30°)	4.5	kJ/m2	ISO 179/1eA
Izod notched impact strength, +23°	5.5	kJ/m2	ISO 180/1A
Izod notched impact strength	4.5	kJ/m2	ISO 180/1A
Temperature	-30	°C	—

Table 2 of 4

1 row

Characteristic	Value	Unit	Method
Density	1140	kg/m3	ASTM D 792

Table 3 of 4

7 rows

Characteristic	Value	Unit	Method
Temperature of deflection under load (1.80 Mpa)	72	°C	ISO 75-1/-2
Temperature of deflection under load (0.45 Mpa)	225	°C	ISO 75-1/-2
Melting temperature (10°C/min)	258	°C	ISO 11357-1/-3
Oxygen index	28	%	ISO 4589-1/-2
Thickness tested	0.8	mm	—
Vicat softening temperature	240	°C	ISO 306
Burning Behavior at thickness	V-2	class	IEC 60695-11-10

Table 4 of 4