Polynil® P270
- Chemical Family
- Polyamides
POLYNIL® P270 is an unreiforced Polyamide 66 (Nylon 66) for extrusion.This 5.3 viscosity Polyamide 66 resin is FDA compliant.
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Polynil
- Polymer Name
- Polyamide 66 (PA 66)
- Flexural Modulus
- 2800.0 - 2800.0 MPa
- Processing Methods
- Extrusion, Film Extrusion
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Film Extrusion
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527 |
| Yield stress | 82 | MPa | ISO 527 |
| Flexural modulus, 23° | 2800 | MPa | ISO 178 |
| Charpy impact strength (+23°) | N | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (+23°) | 8 | kJ/m2 | ISO 179/1eA |
| Strain at Break | min. 50 | % | ISO 527 |
| Izod notched impact strength, +23° | 7 | kJ/m2 | ISO 180/1A |
Table 2 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1140 | kg/m3 | ASTM D 792 |
Table 3 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temperature of deflection under load (1.80 Mpa) | 72 | °C | ISO 75-1/-2 |
| Temperature of deflection under load (0.45 Mpa) | 225 | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 258 | °C | ISO 11357-1/-3 |
| Oxygen index | 28 | % | ISO 4589-1/-2 |
| Thickness tested | 0.8 | mm | — |
| Vicat softening temperature | 240 | °C | ISO 306 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
Table 4 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 8.5 | % | Sim. to ISO 62 |