To catalogue
Nilamid® C3 GF30
- Chemical Family
- Polyamides
Nilit NILAMID® C3 GF30 is a Polyamide 66/6 (Nylon 66/6) compound, 30% glass fiber reinforced, heat stabilized.This compound is intended for injection molding.NILAMID® C3 GF30 is primarily designed for the Automotive industry. It is also suitable for Electrical and Electronic or Industrial & Consumer applications.
Product families
Applications
Applications
- Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications
Automotive & Transportation — Automotive
- Exterior & Body
- Other Automotive Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Nilamid
- Polymer Name
- Polyamide 6/66 (PA 6/66)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 8200.0 - 8200.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- Heat Stabilized
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Automotive Applications
- Consumer Applications
- Electrical/Electronic Applications
- Industrial Applications
- Kitchenware
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1A/1 |
| Yield stress | 175 | MPa | ISO 527 |
| Strain at break | 2.8 | % | ISO 527 |
| Flexural Modulus | 5200 | MPa | ASTM D790 |
| Flexural modulus, 23° | 8200 | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 12 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 50 | kJ/m2 | ISO 179/1eU |
| Charpy impact strength (-30°) | 40 | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (-30°) | 9.5 | kJ/m2 | ISO 179/1eA |
| Izod notched impact strength | 7 | kJ/m2 | ISO 180/1A |
| Izod notched impact strength, +23° | 10 | kJ/m2 | ISO 180/1A |
| Temperature | -30 | °C | — |
Table 2 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Molding shrinkage - parallel | 0.3 | % | ISO 294-4, 2577 |
| Molding shrinkage - normal | 0.5 | % | ISO 294-4, 2577 |
| Density | 1360 | kg/m3 | ISO 1183 |
Table 3 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temperature of deflection under load (1.80 Mpa) | 235 | °C | ISO 75-1/-2 |
| Temperature of deflection under load (0.45 Mpa) | 240 | °C | ISO 75-1/-2 |
| Oxygen index | 24 | % | ISO 4589-1/-2 |
| Thickness tested | 0.8 | mm | — |
| Vicat softening temperature | 225 | °C | ISO 306 |
| Burning Behavior at 1.5 mm nominal thickness | HB | class | IEC 60695-11-10 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
Table 4 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 6 | % | Sim. to ISO 62 |